GI-300 series RTV silicone rubbers are two-component, tin-catalyzed systems that cure at room temperature. They are versatile products that are excellent for electrical potting and encapsulation. They can also be used for prototype or production molds to cast polyester, polyurethane or epoxy parts where flexing is not required. They are low viscosity compounds with a variety of hardnesses. The GI-300 series rubbers are not sensitive to inhibition, meaning they will cure at room temperature over virtually any surface. The speed at which the rubbers harden can be accelerated with special activators. The GI-300 series rubbers are especially useful in those applications where outstanding heat resistance and chemical resistance are required.&&

About

GI-300 series RTV silicone rubbers are two-component, tin-catalyzed systems that cure at room temperature. They are versatile products that are excellent for electrical potting and encapsulation. They can also be used for prototype or production molds to cast polyester, polyurethane or epoxy parts where flexing is not required. They are low viscosity compounds with a variety of hardnesses. The GI-300 series rubbers are not sensitive to inhibition, meaning they will cure at room temperature over virtually any surface. The speed at which the rubbers harden can be accelerated with special activators. The GI-300 series rubbers are especially useful in those applications where outstanding heat resistance and chemical resistance are required.&&

Product Description
Generic	硅橡胶,RTV-2
Material Status	Commercial: Active
Features	Low Viscosity,Low contractility,High Heat Resistance,Solvent resistance
Availabilitys	North America

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.49	g/cm³
Shrinkage rate
Cured	0.15	%

Thermosetting mixed viscosity	Nominal value	Unit	Test method

Uncured Properties	Nominal value	Unit
colour	Beige
viscosity	65 to 75	Pa·s
Curing time	16 to 18	hr
storage stability	60 to 120	min

Cured Properties	Nominal value	Unit	Test method
Shore hardness
Shaw’s A	54 to 64
Shaw’s A	60 to 68
tensile strength	4.48	MPa	ASTM D412
Tensile strain
fracture	100	%	ASTM D412
tear strength	3.50	kN/m	ASTM D624
Arc resistance	125	sec
Electrical strength	23	kV/mm
Relative permittivity
100 Hz	3.70
Volume resistivity	1.0E+13	ohms·cm
Dissipation factor
100 Hz	0.030
Coverage（Cured）	0.672	cm³/g

THERMAL	Nominal value	Unit
Linear coefficient of thermal expansion
MD	1.0E-3	1/℃
Thermal conductivity coefficient	0.29	W/m/K
Operating temperature
Cured	-51 to 218	℃
Thermosetting components
resin	按重量计算的混合比: 10 按容量计算的混合比: 100
Hardening method	按容量计算的混合比: 15 按重量计算的混合比: 1.0
Storage period	26	wk

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.