| About |
|---|
| Novodur® H950 is a very high heat injection molding grade with high gloss surface appearance FEATURES Very high heat resistance High gloss APPLICATIONS Painted exterior automotive mirrors Rear lamp automotive housings Automotive parts&& |
| Product Description | |
|---|---|
| Supplier | INEOS |
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | Good surface appearance,Sprayable,High Heat Resistance |
| Availabilitys | Africa & Middle East ,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 220℃，10 kg | 4.00 | cm³/10min | ISO 1133 |
| Shrinkage rate | 0.50 to 0.70 | % | ISO 294-4 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30℃ | 7.0 | kJ/m² | ISO 179 |
| 23℃ | 16 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | ISO 179 | ||
| -30℃ | 90 | kJ/m² | ISO 179 |
| 23℃ | 140 | kJ/m² | ISO 179 |
| Impact strength of cantilever beam notch | ISO 180/A | ||
| -30℃ | 8.0 | kJ/m² | ISO 180-A |
| 23℃ | 17 | kJ/m² | ISO 180-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, annealed | 108 | ℃ | ISO 75-2/B |
| 1.8 MPa, annealed | 101 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| B50 | 113 | ℃ | ISO 306 |
| Linear coefficient of thermal expansion | |||
| MD | 7.0E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | |||
| 1.5 mm | 37 | kV/mm | IEC 60243-1 |
| Relative permittivity | IEC 60250 | ||
| 100 Hz | 3.20 | IEC 60250 | |
| 1 MHz | 3.00 | IEC 60250 | |
| Dissipation factor | IEC 60250 | ||
| 100 Hz | 6.0E-3 | IEC 60250 | |
| 1 MHz | 0.010 | IEC 60250 | |
| Compared to the leakage tracing index | 600 | V | IEC 60112 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | 110 | MPa | ISO 2039-1 |
| Tensile modulus | 2600 | MPa | ISO 527-2 |
| tensile strength | |||
| Yield, 23 ℃ | 50.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| Yield, 23 ℃ | 2.7 | % | ISO 527-2 |
| Bending modulus | 2600 | MPa | ISO 178 |
| bending strength | 80.0 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Processing (melt) temperature | 230 to 260 | °C | |
| Mold temperature | 60 to 80 | °C | |
| Injection Velocity | 240 | mm/sec | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 4h/80°C |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |