| 30% glass bead reinforced Polyamide 6 with higher stiffness and dimension stability&& |
| Product Description | |
|---|---|
| Supplier | A. Schulman |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Low warping,Good surface appearance,Good Dimensional Stability,Grease resistance,HB |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.36 | g/cm³ | ISO 1183/A |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 2.2 | % | ISO 62 |
| Viscosity number | 145 | cm³/g | ISO 307 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 3.0 | kJ/m² | ISO 179/1eA |
| 23℃ | 5.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 28 | kJ/m² | ISO 179/1eU |
| 23℃ | 35 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 68.0 | ℃ | ISO 75-2/Af |
| 0.45 MPa, unannealed | 180 | ℃ | ISO 75-2/Bf |
| Vicat Softening Temp | |||
| A50 | 215 | ℃ | ISO 306/A50 |
| B50 | 200 | ℃ | ISO 306 |
| Ball pressure test | |||
| 105℃ | Pass | IEC 60695-10-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume resistivity | > 1.0E+13 | ohms·cm | IEC 60093 |
| Compared to the leakage tracing index | 450 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Burning rate | < 100 | mm/min | ISO 3795 |
| Flammability level | IEC 60695-11-10, -20 | ||
| 1.5 mm | HB | IEC 60695-11-10, -20 | |
| 3.0 mm | HB | IEC 60695-11-10, -20 | |
| Glowing wire flammability index | IEC 60695-2-12 | ||
| 1.5 mm | — | ℃ | IEC 60695-2-12 |
| 3.0 mm | — | ℃ | IEC 60695-2-12 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 4000 | MPa | ISO 527-2/1A/1 |
| tensile strength | |||
| fracture | 70.0 | MPa | ISO 527-2/1A/5 |
| Tensile strain | |||
| fracture | 10 | % | ISO 527-2/1A/5 |
| Bending modulus | 3000 | MPa | ISO 178 |
| bending strength | 100 | MPa | ISO 178 |
| Bending strain | 6.5 | % | ISO 178 |
| Ball hardness | |||
| H358/30 | 165 | MPa | ISO 2039-1 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.040 to 0.10 | % | |
| Proposed maximum recycled material ratio | 20 | % | |
| Processing (melt) temperature | 250 to 280 | °C | |
| Mold temperature | 60 to 100 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |