| LNP* THERMOCOMP* 9X10401H is a compound based on Polyphenylsulfone containing proprietary filler(s). Added feature of this grade is: X-Ray Opaque. |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | Shielded X rays |
| Availabilitys | North America,Latin America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | g/cm³ | ASTM D792 | |
| Shrinkage rate | |||
| MD：24 hrs | 0.80 to 1.0 | % | |
| TD：24 hrs | 1.0 to 3.0 | % | |
| Water absorption rate | |||
| 24hr，50% RH | 0.26 | % | ASTM D570 |
| Equilibrium, 23 ℃, 50% RH | 0.47 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| — | 2660 | MPa | ASTM D638 |
| — | 2550 | MPa | ISO 527-1-2 |
| Tensile strength | |||
| yield | 72.0 | MPa | ASTM D638 |
| yield | 71.0 | MPa | ISO 527-2/5 |
| fracture | 57.0 | MPa | ASTM D638 |
| fracture | 57.0 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| yield | 7.0 | % | ASTM D638 |
| yield | 7.0 | % | ISO 527-2/5 |
| fracture | 12 | % | ASTM D638 |
| fracture | 12 | % | ISO 527-2/5 |
| Bending modulus | |||
| 50 mm span | 2720 | MPa | ASTM D790 |
| — | 2570 | MPa | ISO 178 |
| Bending stress | 0.00 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 86 | J/m | ASTM D256 |
| 23℃ | 8.0 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 1600 | J/m | ASTM D4812 |
| 23℃ | 180 | kJ/m² | ISO 180/1U |
| Dart impact equipped with measuring instruments | |||
| 23°C，Total Energy | 34.0 | J | ASTM D3763 |
| — | 29.0 | J | ISO 6603-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 3.2 mm | 214 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 4.0 mm, 64 mm span | 213 | ℃ | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.2 mm | 203 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 4.0 mm, 64 mm span | 200 | ℃ | ISO 75-2/Af |
| Linear coefficient of thermal expansion | |||
| MD：-30~30℃ | 5.3E-5 | 1/℃ | |
| TD：-30~30℃ | 5.3E-5 | 1/℃ |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |