| CABELEC CC6057 conductive concentrate is an electrically conductive concentrate, made from carbon black and a polypropylene copolymer. The concentrate can be diluted at high levels depending on the processing conditions and the targeted specification for the electrical resistivity. Its electrical and mechanical properties are not dependent on atmospheric conditions. Applications CABELEC CC6057 conductive concentrate can be used in extrusion applications such as sheets and corrugated sheets for packaging electronics, where freedom from the hazard of electrostatic discharge is required. CABELEC CC6057 conductive concentrate can also be used for injection moulding applications such as pallets or boxes where it can be diluted at high rates with natural or even recycled polypropylene.&& |
| Product Description | |
|---|---|
| Generic | PP copolymer |
| Material Status | Commercial: Active |
| Features | Conductive,Copolymer |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.13 | g/cm³ | Internal Method |
| Melt Flow Rate | ISO 1133 | ||
| 230℃，10.0kg | 15 | g/10min | ISO 1133 |
| 230℃，21.6kg | 74 | g/10min | ISO 1133 |
| 230℃，5.0kg | 1.0 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ISO 527-2 | ||
| Yield, injection molding | 26.0 | MPa | ISO 527-2 |
| Yield, injection molding | 27.0 | MPa | ISO 527-2 |
| Yield, injection molding | 28.0 | MPa | ISO 527-2 |
| Tensile strain | ISO 527-2 | ||
| Fracture, injection molding | 120 | % | ISO 527-2 |
| Fracture, injection molding | 76 | % | ISO 527-2 |
| Fracture, injection molding | 44 | % | ISO 527-2 |
| Bending modulus | ISO 178 | ||
| injection molding | 1320 | MPa | ISO 178 |
| injection molding | 1380 | MPa | ISO 178 |
| injection molding | 1460 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Notched impact strength of cantilever beam | ISO 180 | ||
| injection molding | 73 | kJ/m² | ISO 180 |
| injection molding | 71 | kJ/m² | ISO 180 |
| injection molding | 67 | kJ/m² | ISO 180 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | Internal Method | ||
| — | 20 | ohms | Internal Method |
| 0.3 mm | 3.0E+5 | ohms | Internal Method |
| 0.3 mm | 2.0E+3 | ohms | Internal Method |
| 0.3 mm | 3.0E+2 | ohms | Internal Method |
| Volume resistivity | 1.0 | ohms·cm | Internal Method |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Barrel rear temperature | 200 | °C | |
| Barrel middle temperature | 200 | °C | |
| Barrel front temperature | 200 | °C | |
| Nozzle temperature | 220 | °C | |
| Mold temperature | 30 | °C | |
| Drying temperature | 80 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Barrel 1 zone temperature | 190 to 220 | °C | |
| Barrel 3 zone temperature | 190 to 220 | °C | |
| Barrel 5 zone temperature | 190 to 220 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Dilution 55% ppc |
| 3. Dilution 50% ppc |
| 4. Dilution 40% ppc |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |