| SUMIKASUPER® LCP E6007AS is a Liquid Crystal Polymer (LCP) material filled with glassinorganic. It is available in Asia Pacific, Europe, or North America for injection molding.&& |
| Product Description | |
|---|---|
| Supplier | Sumitomo |
| Generic | 液态聚合物 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,Good heat aging resistance,Good Dimensional Stability,Low Viscosity,High Heat Resistance,Good bond,Solvent resistance,Antistatic property,Welding |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.63 | g/cm³ | ASTM D792 |
| Shrinkage rate | Internal Method | ||
| MD | 0.31 | % | Internal Method |
| TD | 1.1 | % | Internal Method |
| Water absorption rate | |||
| saturated | 0.020 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 121 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 6.8 | % | ASTM D638 |
| Bending modulus | |||
| 23℃ | 9800 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 23 ℃ | 126 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Notched impact strength of cantilever beam | |||
| 6.4 mm | 340 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 274 | ℃ | ASTM D648 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Soldering Resistance | 300 | ℃ | Internal Method |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 to 150 | °C | |
| Drying time | 3.0 | hr | |
| Proposed maximum recycled material ratio | 30 | % | |
| Barrel rear temperature | 300 to 320 | °C | |
| Barrel middle temperature | 320 to 350 | °C | |
| Barrel front temperature | 340 to 370 | °C | |
| Nozzle temperature | 340 to 370 | °C | |
| Processing (melt) temperature | 350 | °C | |
| Mold temperature | 70 to 160 | °C | |
| Injection pressure | 78.0 to 157 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |