SABIC® LLDPE 318BJ (Wire & Cable Extrusion)

About
SABIC® LLDPE 318BJ is a butene Linear Low Density Polyethylene natural resin typically used for wire and cable applications. SABIC® LLDPE 318BJ contains a high level of antioxidants and does not contain any antiblock and/or slip agents. It exhibits good Environmental Stress Crack Resistance (ESCR). SABIC® LLDPE 318BJ is typically used as base resin for insulation and jacketing applications. Applications Telecommunication and Power cable (LV, MV, HV) jacketing. Halogen-free flame retardant (HFFR) compounds. One-step or two-steps silane crosslinkable for cable insulation. The product mentioned herein is in particular not tested and therefore not validated for use in pharmaceutical/medical applications.&&

About

SABIC® LLDPE 318BJ is a butene Linear Low Density Polyethylene natural resin typically used for wire and cable applications. SABIC® LLDPE 318BJ contains a high level of antioxidants and does not contain any antiblock and/or slip agents. It exhibits good Environmental Stress Crack Resistance (ESCR). SABIC® LLDPE 318BJ is typically used as base resin for insulation and jacketing applications. Applications Telecommunication and Power cable (LV, MV, HV) jacketing. Halogen-free flame retardant (HFFR) compounds. One-step or two-steps silane crosslinkable for cable insulation. The product mentioned herein is in particular not tested and therefore not validated for use in pharmaceutical/medical applications.&&

Product Description
Supplier	SABIC
Generic	Linear low density polyethylene
Material Status	Commercial: Active
Features	Inoxidizability,Low density,Butylene copolymer,High ESCR
Availabilitys	Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.918	g/cm³	ISO 1183/A
Melt Flow Rate
190℃，2.16kg	2.8	g/10min	ISO 1133

film	Nominal value	Unit	Test method
film thickness
test	20	µm
Elastic Recovery (cast film, 20.0 µ m)	52	%	ASTM D5459
Corrosion Function Resistance – Cast thin film (20.0 µ m)	2.00	J	ASTM D5748
Stress Retention (cast film, 20.0 µ m)	78	%	ASTM D5459

THERMAL	Nominal value	Unit	Test method
Vicat Softening Temp	102	℃	ISO 306/A
Melting temperature
DSC	121	℃	Internal Method

optical performance	Nominal value	Unit	Test method
gloss
45 °, 20 µ m, cast thin film	91		ASTM D2457
Haze
20.0 µ m, cast thin film	2.1	%	ASTM D1003

Supplementary information	Nominal value	Unit	Test method
Drop hammer impact
20.0 µ m, cast thin film	26.0	J/cm	ISO 7765-2
tear strength
TD，20 µm	140.0	kN/m	ISO 6383-2
memo_intro

Process Conditions
Extrusion	Nominal value	Unit	Test method
Melt temperature	250 to 300	°C

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.