| About |
|---|
| Description: MARPOL® LL6F 802 is a hexene LLDPE resin with good stiffness at thin gauges, good drawdown and excellent processability. This resin is suitable for blown and cast film applications and for blends with LLDPE or HDPE. Recommended Applications Stretch wrap, overwrap, coextrusions, blown film and cast film&& |
| Product Description | |
|---|---|
| Generic | Linear low density polyethylene |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,Good dissection,Hexene copolymers |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.919 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 2.0 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| friction coefficient | > 1.0 | ASTM D1894 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Secant modulus | ASTM D882 | ||
| 1% secant, MD | 200 | MPa | ASTM D882 |
| 1% secant, TD | 214 | MPa | ASTM D882 |
| tensile strength | ASTM D882 | ||
| MD, fracture | 42.7 | MPa | ASTM D882 |
| TD, fracture | 33.1 | MPa | ASTM D882 |
| Tensile strain | ASTM D882 | ||
| MD, fracture | 580 | % | ASTM D882 |
| TD, fracture | 780 | % | ASTM D882 |
| Drop hammer impact | 140 | g | ASTM D1709 |
| Elmandorf tear strength | ASTM D1922 | ||
| MD | 300 | g | ASTM D1922 |
| TD | 550 | g | ASTM D1922 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 60° | 140 | ASTM D2457 | |
| Haze | 3.0 | % | ASTM D1003 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |