| Rilsamid® AESNO P401 TL resin is a natural polyamide. This grade is plasticized and designed for tube extrusion. Rilsamid® AESNO P401 TL resin falls into the PA12-HIPHL category according to DIN 73378. |
| Product Description | |
|---|---|
| Supplier | Arkema |
| Generic | PA12 |
| Material Status | Commercial: Active |
| Features | Plasticizing |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.03 | g/cm³ | |
| Melt Volume Rate | |||
| 235℃，5 kg | 13.0 | cm³/10min | |
| Water absorption rate | |||
| Saturation, 23 ℃ | 1.2 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | — | MPa | |
| tensile strength | |||
| 50% strain | — | MPa | |
| Tensile strain | |||
| fracture | — | % |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 4.0 | kJ/m² | |
| 23 ℃, localized fracture | 46 | kJ/m² | |
| 23℃ | — | ||
| Charpy Unnotch Impact strength | |||
| -30℃ | 无断裂 | ||
| 23℃ | 无断裂 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 174 | ℃ | |
| Linear coefficient of thermal expansion | |||
| MD | |||
| 1.60 mm | 1.5E-4 | cm/cm/℃ | |
| 3.20 mm | 1.5E-4 | cm/cm/℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | 41 | kV/mm | |
| Compared to the leakage tracing index | 600 | V |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Extreme oxygen index | 20 | % |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |