DuClear® QU 80 A

About
Description DuClear QU 80 A is a polypropylene random copolymer, suitable for injection moulding applications The product is clarified and contains an anti-electrostatic agent. DuClear QU 80 A features a very good transparency and aesthetic appearance, a good balance of stiffness and impact strength, good organoleptics, low blooming, high melt flow, and energy & cycle time savings. Applications DuClear QU 80 A is suitable for: high-speed injection moulding, thin-walled packaging, containers, and houseware.&&

About

Description DuClear QU 80 A is a polypropylene random copolymer, suitable for injection moulding applications The product is clarified and contains an anti-electrostatic agent. DuClear QU 80 A features a very good transparency and aesthetic appearance, a good balance of stiffness and impact strength, good organoleptics, low blooming, high melt flow, and energy & cycle time savings. Applications DuClear QU 80 A is suitable for: high-speed injection moulding, thin-walled packaging, containers, and houseware.&&

Product Description
Generic	PP copolymer
Material Status	Commercial: Active
Features	Good Clarity,Good surface appearance,High liquidity,Food contact compliance,Good sensory characteristics.,Random copolymer,Antistatic property
Availabilitys	Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.910	g/cm³	ISO 1183
Melt Flow Rate
230℃，2.16kg	40	g/10min	ISO 1133

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus	1100	MPa	ISO 527-1-2
tensile strength
yield	28.0	MPa	ISO 527-2/50
Tensile strain			ISO 527-2/50
yield	12	%	ISO 527-2/50
fracture	> 50	%	ISO 527-2/50

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength			ISO 179/1eA
0℃	1.8	kJ/m²	ISO 179/1eA
23℃	5.0	kJ/m²	ISO 179/1eA
Charpy Unnotch Impact strength			ISO 179/1eU
0℃	60	kJ/m²	ISO 179/1eU
23℃	180	kJ/m²	ISO 179/1eU
Impact strength of cantilever beam notch			ISO 180/1A
0℃	2.0	kJ/m²	ISO 180-1A
23℃	4.5	kJ/m²	ISO 180-1A

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	75.0	℃	ISO 75-2/B
1.8 MPa, unannealed	50.0	℃	ISO 75-2/A
Vicat Softening Temp
—	130	℃	ISO 306/A
—	72.0	℃	ISO 306/B
Melting temperature
DSC	151	℃	ISO 3146

optical performance	Nominal value	Unit	Test method
Haze
1000 µm	8.0	%	ASTM D1003

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.