| About |
|---|
| Clariant PBT PBT-1100G30TF15是一种聚丁烯对苯二甲酸酯(PBT)材料,含有的填充物为30% 玻璃纤维增强材料。 该产品在北美洲有供货,加工方式为:注射成型。 Clariant PBT PBT-1100G30TF15的主要特性有: 阻燃/额定火焰 高强度 坚硬 良好的尺寸稳定性 良好的韧性 典型应用领域包括: 电线电缆 工程/工业配件&& |
| Product Description | |
|---|---|
| Supplier | Clariant |
| Generic | polybutylene terephthalate |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good flexibility,Good Dimensional Stability,Low coefficient of friction,High Heat Resistance,Lubricating,Good wear resistance,Solvent resistance,HB |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.66 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.50 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr | 0.040 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 3.2mm | 69 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed | 221 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 207 | ℃ | ASTM D648 |
| Melting temperature | 220 to 225 | ℃ | |
| Linear coefficient of thermal expansion | |||
| MD | 2.3E-5 | 1/℃ | ASTM D696 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric strength | 18 | kV/mm | ASTM D149 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.79 mm | HB | UL 94 | |
| 1.60 mm | HB | UL 94 | |
| 3.20 mm | HB | UL 94 | |
| 6.40 mm | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | ASTM D785 | ||
| M-level | 82 | ASTM D785 | |
| R-level | 118 | ASTM D785 | |
| tensile strength | 114 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 3.0 | % | ASTM D638 |
| Bending modulus | 8620 | MPa | ASTM D790 |
| bending strength | 150 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 121 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Barrel rear temperature | 232 to 274 | °C | |
| Barrel middle temperature | 232 to 274 | °C | |
| Barrel front temperature | 232 to 274 | °C | |
| Processing (melt) temperature | 232 to 246 | °C | |
| Melt temperature (target) | 241 | °C | |
| Mold temperature | 66 to 82 | °C | |
| Injection speed | 快速 | ||
| Back pressure | 0.345 to 0.689 | MPa | |
| Screw speed | 20 to 80 | rpm | |
| Cushion | 3.18 to 6.35 | mm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |