Ultraform® S 2320 003 UNC Q600

About
Ultraform S 2320 003 UNC Q600 is an easy flowing and rapidly freezing injection molding POM grade. Contains a mold release agent. Applications Typical applications include difficult, thin-walled parts.&&

Product Description
Supplier	BASF
Generic	Copolymer Polyformaldehyde
Material Status	Commercial: Active
Features	Good liquidity,Good stripping performance,Copolymer
Availabilitys	North America
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.40	g/cm³	ASTM D792
Density	1.40	g/cm³	ISO 1183
Melt Volume Rate
190℃，2.16 kg	11.0	cm³/10min	ISO 1133
Shrinkage rate			ISO 294-4
MD：3.2 mm	2.0	%
TD	2.1	%	ISO 294-4
MD	2.1	%	ISO 294-4
Water absorption rate
Saturation, 23 ℃	0.80	%	ISO 62
saturated	0.80	%	ASTM D570
Equilibrium, 23 ℃, 50% RH	0.20	%	ISO 62
Balance, 50% RH	0.20	%	ASTM D570

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus
23℃	2700	MPa	ISO 527-2
tensile strength			ISO 527-2
Yield, 23 ℃	65.0	MPa	ASTM D638
Yield, -40 ℃	93.0	MPa	ISO 527-2
Yield, 23 ℃	65.0	MPa	ISO 527-2
Yield, 80 ℃	33.0	MPa	ISO 527-2
Tensile strain
Yield, 23 ℃	9.0	%	ISO 527-2
Yield, 23 ℃	9.0	%	ASTM D638
Nominal tensile fracture strain
23℃	28	%	ISO 527-2
Tensile Creep Modulus（1 hr）	1900	MPa	ISO 899-1
Tensile creep modulus
1000 hr	1300	MPa	ISO 899-1
Bending modulus
23℃	2620	MPa	ASTM D790

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength			ISO 179
-30℃	5.0	kJ/m²	ISO 179
23℃	5.5	kJ/m²	ISO 179
Charpy Unnotch Impact strength			ISO 179
-30℃	170	kJ/m²	ISO 179
23℃	180	kJ/m²	ISO 179
Impact strength of cantilever beam notch			ASTM D256
-40℃	50	J/m	ASTM D256
23℃	60	J/m	ASTM D256

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	100	℃	ISO 75-2/A
1.8 MPa, unannealed	110	℃	ASTM D648
0.45 MPa, unannealed	156	℃	ISO 75-2/B
0.45 MPa, unannealed	160	℃	ASTM D648
Melting peak temperature	167	℃	ASTM D3418
Melting temperature
DSC	167	℃	ISO 3146
Linear coefficient of thermal expansion
MD	6.0E-5	1/℃	ASTM E831
MD	1.1E-4	1/℃

Electrical performance	Nominal value	Unit	Test method
Surface resistivity	1.0E+13	ohms	ASTM D257
Surface resistivity	1.0E+13	ohms	IEC 60093
Volume resistivity	1.0E+13	ohms·cm	IEC 60093
1.50 mm	1.0E+13	ohms·cm	ASTM D257
Dielectric strength	40	kV/mm	IEC 60243-1
Dielectric constant			IEC 60250
100 Hz	3.80		IEC 60250
1 MHz	3.80		IEC 60250
Dissipation factor			IEC 60250
100 Hz	1.0E-3		IEC 60250
1 MHz	5.0E-3		IEC 60250
Compared to the leakage tracing index	600	V	IEC 60112

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	80 to 110	°C
Drying time	2.0 to 4.0	hr
Recommended maximum moisture content	0.15	%
Processing (melt) temperature	190 to 230	°C
Mold temperature	60 to 120	°C
Injection pressure	3.50 to 7.00	MPa

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.