| Product Description | |
|---|---|
| Supplier | Wanhua |
| Generic | Polycarbonate |
| Material Status | Commercial: Negative |
| Features | High liquidity |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ASTM D792 |
| Water absorption rate | |||
| 23℃，50%RH | 0.2 | % | ASTM D570 |
| Melt index | |||
| 300℃，1.2kg | 10 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| 50mm/min | 65 | MPa | ASTM D638 |
| Tensile modulus | |||
| 1mm/min | 2300 | MPa | ASTM D638 |
| elongation at break | |||
| 50mm/min | 110 | % | ASTM D638 |
| bending strength | |||
| 2mm/min | 95 | MPa | ASTM D790 |
| Bending modulus | |||
| 2mm/min | 2300 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 810 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.82Mpa,3.2mm | 126 | ℃ | ASTM D648 |
| Vicat Softening Temp | |||
| 120℃/h，50N | 146 | ℃ | ASTM D1525 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 3.0mm | V-0 | UL 94 | |
| Glowing wire flammability index | |||
| 3.0mm | 960 | ℃ | IEC 60695-2-12 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.00E+15 | ohms | IEC 60093 |
| Volume resistivity | 1.00E+14 | IEC 60093 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |