| About |
|---|
| AKROLEN® PP GFM 25/15 LA black (3143) is a 25% glass fibre reinforced, 15% mineralfilled, laser markable polypropylene with good surface and dimensional stability. Mainly thin wall housings for electronic parts in the automotive industry.&& |
| Product Description | |
|---|---|
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | Good surface appearance,Good Dimensional Stability,Laser engraving |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.21 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 230℃，2.16 kg | 13.5 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| TD | 0.50 | % | |
| MD | 0.20 | % | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 11 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| -30℃ | 45 | kJ/m² | |
| 23℃ | 42 | kJ/m² | |
| Notched impact strength of cantilever beam | |||
| 23℃ | 10 | kJ/m² | ISO 180/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 163 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 150 | ℃ | ISO 75-2/A |
| Melting temperature | 167 | ℃ | DIN EN 11357-1 |
| Linear coefficient of thermal expansion | |||
| MD：23~80℃ | 2.0E-5 | 1/℃ | |
| TD：23~80℃ | 1.3E-4 | 1/℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | |||
| 3 mm | 18 | kV/mm | IEC 60243-1 |
| Compared to the leakage tracing index | |||
| Solution A | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | HB | UL 94 | |
| Burning rate | |||
| 1 mm | < 100 | mm/min | FMVSS 302 |
| Glowing wire flammability index | |||
| 2.0 mm | 750 | ℃ | IEC 60695-2-12 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Ash Content | 40 | % | ISO 1172 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | |||
| H358/30 | 100 | MPa | ISO 2039-1 |
| Tensile modulus | 6500 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 75.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| fracture | 3.5 | % | ISO 527-2/50 |
| Bending modulus | 6600 | MPa | ISO 178 |
| bending strength | 105 | MPa | ISO 178 |
| Fracture bending strain | 3.6 | % | ISO 178 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 3. 2 mm/min |
| 4. 10°C/min |
| 5. >1 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |