| About |
|---|
| Product Description | |
|---|---|
| Material Status | Commercial: Negative |
| Features | Arc resistance,Insulation,Solvent resistance,Good wear resistance,High Heat Resistance,Self-lubricating,Flame Characteristics |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.68 | g/cm³ | ISO 1183 |
| Forming shrinkage rate | |||
| 0.2 | % | GB/T 15585 | |
| 0.8 | % | GB/T 15585 | |
| Water absorption rate | 0.02 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 140 | MPa | ISO 527 |
| elongation at break | 1.6 | % | ISO 527 |
| bending strength | 245 | MPa | ISO 178 |
| Bending modulus | 12 | GPa | ISO 178 |
| Rockwell hardness | 112 | R | ISO 2039-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 12.5 | KJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 280 | ℃ | ISO 11357 |
| Hot deformation temperature | |||
| 1.8MPa | 260 | ℃ | ISO 75 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+14 | ohm·cm | IEC 60093 |
| Dielectric constant | |||
| 1MHz | 3.8 | IEC 60250 | |
| Dielectric strength | |||
| 1 mm | 16 | kV/mm | IEC 60243 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| Cylinder temperature | 300 – 330 | ℃ | |
| Mold temperature | 100 – 130 | ℃ | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |