| About |
|---|
| PRL PC-FR2-TFE is a Polycarbonate (PC) product. It can be processed by injection molding and is available in North America. Characteristics include: Flame Rated RoHS Compliant Flame Retardant Lubricated&& |
| Product Description | |
|---|---|
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Flame Characteristics,Lubricating,V-2,V-0 |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.26 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 9.0 to 16 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.50 to 1.0 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Fracture, 3.18 mm | 56.9 | MPa | ASTM D638 |
| Yield, 3.17 mm | 56.9 | MPa | ASTM D638 |
| Tensile strain | |||
| Yield, 3.18 mm | > 10 | % | ASTM D638 |
| Bending modulus | |||
| 3.17 mm | 2410 | MPa | ASTM D790 |
| bending strength | |||
| 3.18 mm | 82.7 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 120 | J/m | ASTM D256 |
| Drop hammer impact | |||
| 3.2 mm | 36.2 | J | ASTM D3029 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 129 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 3.2 mm | 135 | ℃ | ASTM D648 |
| 1.6 mm | 80.0 | ℃ | UL 746 |
| 3.0 mm | 80.0 | ℃ | UL 746 |
| Relative temperature index | |||
| Electrical performance | UL 746 | ||
| Strength mechanical performance | UL 746 | ||
| Impact mechanical performance | UL 746 | ||
| 1.6 mm | 80.0 | ℃ | UL 746 |
| 3.0 mm | 80.0 | ℃ | UL 746 |
| 1.6 mm | 80.0 | ℃ | UL 746 |
| 3.0 mm | 80.0 | ℃ | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.60 mm | V-2 | UL 94 | |
| 3.00 mm | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 118 to 124 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Drying time, maximum | 8.0 | hr | |
| Barrel rear temperature | 271 to 293 | °C | |
| Barrel middle temperature | 282 to 304 | °C | |
| Barrel front temperature | 293 to 316 | °C | |
| Processing (melt) temperature | 288 to 316 | °C | |
| Mold temperature | 77 to 99 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |