| About |
|---|
| Product Description | |
|---|---|
| Material Status | Commercial: Negative |
| Features | Good Dimensional Stability,Good liquidity,Solvent resistance,Flame Characteristics,Good flexibility |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.73 | g/cm³ | ISO 1183 |
| Forming shrinkage rate | |||
| 0.3 | % | GB/T 15585 | |
| 0.7 | % | GB/T 15585 | |
| Water absorption rate | 0.02 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 145 | MPa | ISO 527 |
| elongation at break | 1.2 | % | ISO 527 |
| bending strength | 210 | MPa | ISO 178 |
| Bending modulus | 11 | GPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 7.5 | KJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 280 | ℃ | ISO11357 |
| Hot deformation temperature | |||
| 1.8MPa | 260 | ℃ | ISO 75 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+14 | ohm·m | IEC60093 |
| Dielectric strength | |||
| 1.0mm | 18 | kV/mm | IEC60243 |
| Dielectric constant | |||
| 1MHz | 5 | IEC60250 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 130 – 150 | ℃ | |
| Drying time | 4 – 8 | hrs | |
| Mold temperature | 120 – 150 | ℃ | |
| Front temperature | 290 – 300 | ℃ | |
| Mid section temperature | 300 – 320 | ℃ | |
| Post stage temperature | 310 – 330 | ℃ | |
| Nozzle temperature | 310 – 330 | ℃ | |
| Injection pressure | 80 – 150 | ℃（70-95%） | |
| Injection molding speed | 中速 – 高速 | ||
| Maintaining pressure | 30 – 70 | MPa（20-45%） | |
| Measurement | 5 – 10 | mm | |
| Relaxation | 3 – 5 | mm | |
| Screw speed | 50 – 120 | rpm | |
| Backpressure pressure | 0.2 – 5 | MPa | |
| Post treatment temperature | 160 – 180 | ℃ | |
| Post processing time | 4 – 8 | hrs | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |