| About |
|---|
| Eltex® PF6012KJ is a metallocene LLDPE resin produced in Europe. Applications Eltex® PF6012KJ has been developed for use in highly technical film like food packaging, lamination, and other thin film applications where superior mechanical and sealing performance is required. In addition, Eltex® PF6012KJ offers easy extrudability and distinctive sealing properties. Benefits and Features Eltex® PF6012KJ is a polyethylene copolymer containing hexene-1 as the comonomer produced with a metallocene catalyst. It offers the following properties: Outstanding impact strength Low blocking for the film together with low abrasive character for the extrusion equipment Very low sealing initiation temperature Excellent Hot Tack strength, particularly advantageous for HFFS packaging lines Very good bubble stability and extrudability similar to best LLDPE blown film grade Properties ideally balanced in machine and transverse directions Eltex® PF6012KJ is formulated with slip and antiblocking agents that offer high slip with easy opening properties. Addition of other polymers, masterbatches and pigments may alter film slip and antiblock performance.&& |
| Product Description | |
|---|---|
| Supplier | INEOS |
| Generic | mLLDPE |
| Material Status | Commercial: Active |
| Features | Excellent Processability,High impact resistance,Smoothness,High anti-blocking,Food contact compliance,Inoxidizability,Low density,Copolymer,Hexene copolymers,Low temperature heat sealing |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.913 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 1.3 | g/10min | ISO 1133 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 25 | µm | |
| Tensile modulus | ISO 527-3 | ||
| 1% secant, MD, 25 µ m, blow molded film | 140 | MPa | ISO 527-3 |
| 1% secant, TD, 25 µ m, blow molded film | 140 | MPa | ISO 527-3 |
| tensile strength | ISO 527-3 | ||
| MD, yield, 25 µ m, blow molded film | 8.00 | MPa | ISO 527-3 |
| TD, yield, 25 µ m, blow molded film | 8.00 | MPa | ISO 527-3 |
| MD, fracture, 25 µ m, blow molded film | 65.0 | MPa | ISO 527-3 |
| TD, fracture, 25 µ m, blow molded film | 64.0 | MPa | ISO 527-3 |
| Tensile strain | ISO 527-3 | ||
| MD, fracture, 25 µ m, blow molded film | 480 | % | ISO 527-3 |
| TD, fracture, 25 µ m, blow molded film | 610 | % | ISO 527-3 |
| Drop hammer impact | |||
| 25 µ m, blow molded film | > 1600 | g | ASTM D1709-A |
| Elmandorf tear strength | ASTM D1922 | ||
| MD: 25 µ m, blow molded film | 180 | g | ASTM D1922 |
| TD: 25 µ m, blow molded film | 360 | g | ASTM D1922 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | |||
| DSC | 97.0 to 114 | ℃ | Internal Method |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45 °, 25 µ m, blow molded film | 79 | ASTM D2457 | |
| Haze | |||
| 25 µ m, blow molded film | 4.0 | % | ASTM D1003 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 190 to 230 | °C | |
| Notes |
|---|
| 1. Silica |
| 2. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |