| High Barrier Differentially Coated Film Biaxially oriented polypropylene (BOPP) film coated on one side with a high barrier aqueous dispersion of polyvinylidene chloride (PVdC) copolymer, the other side coated with an aqueous acrylic dispersion. RDU85/100 are suitable for use as a single film or in laminations for overwrapping and form-fill-seal packaging especially in the bakery, cookie and confectionery industries.&& |
| Product Description | |
|---|---|
| Generic | PP Alloy |
| Material Status | Commercial: Active |
| Features | Good heat sealing,High impact resistance,Good Printability,Food contact compliance,Poor moisture permeability,low-temperature impact resistance,Puncture Resistant |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Shrinkage rate | Internal Method | ||
| MD：121℃，1 min | 4.0 | % | Internal Method |
| MD：129℃，1 min | 7.0 | % | Internal Method |
| TD：129℃，1 min | 1.0 | % | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| friction coefficient | ASTM D1894 | ||
| With oneself – dynamic, outer/outer layers | 0.20 to 0.30 | ASTM D1894 | |
| Compared to itself – static, outer/outer layers | 0.20 to 0.30 | ASTM D1894 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 2200 | µm | |
| Sealing emphasis | Internal Method | ||
| — | 0.15 | N/mm | Internal Method |
| — | 0.15 | N/mm | Internal Method |
| Initial sealing temperature | Internal Method | ||
| — | 104 to 146 | ℃ | Internal Method |
| — | 85.0 to 146 | ℃ | Internal Method |
| Oxygen permeability | ASTM F1927 | ||
| 23℃，85% RH | 0.16 | cm³·mm/m²/atm/24 hr | ASTM F1927 |
| 25℃，0% RH | 0.16 | cm³·mm/m²/atm/24 hr | ASTM F1927 |
| Water vapor transmittance | |||
| 38℃，90% RH | 4.0 | g/m²/24 hr | ASTM F1770 |
| dosage | 51.0 | m²/kg | Internal Method |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45° | 100 | ASTM D2457 | |
| Haze | 2.0 to 3.0 | % | ASTM D1003 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. PVdC/PVdC; 265°F; 2secs; 15psi |
| 3. Acrylic/Acrylic; 265°F; 2secs; 15psi |
| 4. Acrylic/Acrylic; 2secs; 15psi |
| 5. PVdC/PVdC; 2secs; 15psi |
| 6. Wide angle; 2.5° |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |