| About |
|---|
| PRIMACOR™ 1430 is an ethylene acrylic acid copolymer that provides good sealability, hot tack and excellent adhesion to polar (foil, nylon, etc.) materials. It also provides excellent toughness, clarity and tear resistance. Adhesive layer of sealant layer in flexible packaging structures For blown or cast film extrusion Used where adhesion to nylon or foil is desired Complies with: U.S. FDA 21 CFR 177.1310(a)(1) EU, No 10/2011 Consult the regulations for complete details.&& |
| Product Description | |
|---|---|
| Supplier | DOW |
| Generic | EAA |
| Material Status | Commercial: Negative |
| Availabilitys | North America,Latin America,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.930 | g/cm³ | ASTM D792 , ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 5.0 | g/10min | ASTM D1238，ISO 1133 |
| Co monomer content | 9.7 | % | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield, molding | 7.67 | MPa | ASTM D638 |
| Yield, molding | 7.67 | MPa | ISO 527-2/508 |
| Fracture, molded | 19.5 | MPa | ASTM D638 |
| Fracture, molded | 19.5 | MPa | ISO 527-2/508 |
| Tensile strain | |||
| Fracture, molded | 580 | % | ASTM D638 |
| Fracture, molded | 580 | % | ISO 527-2/508 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| MD, yield, 51 µ m | 10.4 | MPa | ASTM D882 |
| TD, yield, 51 µ m | 10.2 | MPa | ASTM D882 |
| MD, yield, 51 µ m | 10.4 | MPa | ISO 527-3 |
| TD, yield, 51 µ m | 10.2 | MPa | ISO 527-3 |
| MD, fracture, 51 µ m | 30.6 | MPa | ASTM D882 , ISO 527-3 |
| TD, fracture, 51 µ m | 31.0 | MPa | ASTM D882 , ISO 527-3 |
| Tensile strain | ASTM D882 , ISO 527-3 | ||
| MD, fracture, 51 µ m | 420 | % | ASTM D882 , ISO 527-3 |
| TD, fracture, 51 µ m | 470 | % | ASTM D882 , ISO 527-3 |
| Elmandorf tear strength | |||
| MD：51 µm | 470 | g | ASTM D1922 |
| TD：51 µm | 730 | g | ASTM D1922 |
| MD：51 µm | 2100 | N | ISO 6383-2 |
| TD：51 µm | 3300 | N | ISO 6383-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 76.1 | ℃ | ASTM D1525 , ISO 306 |
| Melting temperature | |||
| DSC | 96.1 | ℃ | Internal Method |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45°，50.8 µm | 74 | ASTM D2457 | |
| Haze | |||
| 50.8 µm | 4.0 | % | ASTM D1003 |
| 50.8 µm | 4.0 | % | ISO 14782 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Comonomer content measured by a proprietary method that has equivalent accuracy as compared to ASTM D 4094. |
| 3. 20 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |