| About |
|---|
| TES J-4/35 is a Polyamide 612 (Nylon 612) product filled with 35% glass fiber. It can be processed by injection molding and is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Applications of TES J-4/35 include engineering/industrial parts, automotive, electrical/electronic applications, furniture and handles. Characteristics include: RoHS Compliant Chemical Resistant Good Stiffness Heat Resistant High Strength&& |
| Product Description | |
|---|---|
| Generic | PA612 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,High impact resistance,High Heat Resistance,Solvent resistance,Low moisture absorption |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.34 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD | 0.20 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr | 0.20 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 130 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 199 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 210 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| MD | 2.5E-5 | 1/℃ | ASTM D696 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+14 | ohms | ASTM D257 |
| Volume resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric strength | 20 | kV/mm | ASTM D149 |
| Dielectric constant | ASTM D150 | ||
| 1 kHz | 3.70 | ASTM D150 | |
| 1 MHz | 3.40 | ASTM D150 | |
| Dissipation factor | ASTM D150 | ||
| 1 kHz | 0.024 | ASTM D150 | |
| 1 MHz | 0.016 | ASTM D150 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 9650 | MPa | ASTM D638 |
| tensile strength | |||
| yield | 172 | MPa | ASTM D638 |
| Tensile strain | |||
| yield | 5.0 | % | ASTM D638 |
| Bending modulus | 9310 | MPa | ASTM D790 |
| bending strength | |||
| yield | 248 | MPa | ASTM D790 |
| compressive strength | 159 | MPa | ASTM D695 |
| shear strength | 65.5 | MPa | ASTM D732 |
| Rockwell hardness | |||
| E-level | 40 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 74 to 104 | °C | |
| Drying time | 2.0 to 16 | hr | |
| Barrel rear temperature | 271 to 282 | °C | |
| Barrel middle temperature | 277 to 288 | °C | |
| Barrel front temperature | 266 to 277 | °C | |
| Nozzle temperature | 260 to 271 | °C | |
| Processing (melt) temperature | 271 to 282 | °C | |
| Mold temperature | 54 to 82 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |