| About |
|---|
| LNP COLORCOMP J1000 is a compound based on Polyethersulfone resin.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PES |
| Material Status | Commercial: Active |
| Features | V-0 |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.37 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| MD | 1.0 | % | Internal Method |
| Water absorption rate | |||
| 23℃，24hr | 0.60 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2700 | MPa | ISO 527-1-2 |
| tensile strength | ISO 527-2/50 | ||
| yield | 91.0 | MPa | ISO 527-2/50 |
| fracture | 67.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 6.8 | % | ISO 527-2/50 |
| Bending modulus | 2600 | MPa | ISO 178 |
| bending strength | 128 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 7.0 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 无断裂 | ISO 180/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 64 mm span | 216 | ℃ | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 64 mm span | 201 | ℃ | ISO 75-2/Af |
| Linear coefficient of thermal expansion | ISO 11359-2 | ||
| MD：23~60℃ | 5.9E-5 | 1/℃ | ISO 11359-2 |
| TD：23~60℃ | 5.9E-5 | 1/℃ | ISO 11359-2 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.50 mm | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 121 to 149 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.050 | % | |
| Barrel rear temperature | 343 to 354 | °C | |
| Barrel middle temperature | 360 to 371 | °C | |
| Barrel front temperature | 371 to 382 | °C | |
| Processing (melt) temperature | 354 to 371 | °C | |
| Mold temperature | 138 to 149 | °C | |
| Back pressure | 0.344 to 0.689 | MPa | |
| Screw speed | 60 to 100 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 3. at Yield |
| 4. 80*10*4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |