| About |
|---|
| A speciality thermoplastic polyolefin resin designed for injection or extrusion automotive applications with low melt and excellent low temperature impact.&& |
| Product Description | |
|---|---|
| Supplier | ExxonMobil |
| Generic | Polyolefin Elastomer |
| Material Status | Commercial: Active |
| Features | Low liquidity,High impact resistance |
| Availabilitys | Africa & Middle East ,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 1.0 | g/10min | ISO 1133 |
| Melt Volume Rate | |||
| 230℃，2.16 kg | 1.50 | cm³/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 1150 | MPa | ISO 527-2 |
| tensile strength | |||
| yield | 25.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| yield | 10 | % | ISO 527-2 |
| Bending modulus | 1100 | MPa | ISO 178 |
| bending strength | 31.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20 ℃, completely fractured | 3.0 | kJ/m² | |
| 0 ℃, completely fractured | 4.0 | kJ/m² | |
| 23 ℃, localized fracture | 25 | kJ/m² | |
| Impact strength of cantilever beam notch | |||
| 23 ℃, localized fracture | 27 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 76.0 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 48.0 | ℃ | ISO 75-2/A |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |