| Features and Benefits Proprietary polymer and catalyst system enables the manufacture of optically clear finished parts Phosphorous-free and silica-free formulation reduces the potential for contamination Low extractables, low outgassing, and low particle generation for ultra high purity applications Excellent temperature resistance optimizes performance in extreme environments (continuous, in-service temperatures to 300°C with peaks up to 350°C) Excellent compression set offers enhanced sealing force retention and seal life Proportionate polymer and catalyst package simplifies the mixing process Smaller, easy to store packages for cleanroom handling&& |
| Product Description | |
|---|---|
| Generic | PFE |
| Material Status | Commercial: Active |
| Features | Low extract,High purity,Good Compression Set,High Heat Resistance,Low odor,Low to no phosphorus content |
| Availabilitys | North America,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 2.00 | g/cm³ | |
| Mooney viscosity | |||
| ML 1+10，121℃ | 80 | MU | |
| Fluorine content | 72 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s A | 60 | ASTM D2240 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 18.3 | MPa | ASTM D412 |
| 100% strain | 1.69 | MPa | ASTM D412 |
| Tensile strain | |||
| fracture | 300 | % | ASTM D412 |
| Compression deformation | |||
| 200℃，22 hr | 8.0 | % | |
| 200℃，70 hr | 16 | % | |
| 200℃，168 hr | 20 | % | |
| 200℃，336 hr | 25 | % | |
| 250℃，22 hr | 15 | % | |
| 250℃，70 hr | 19 | % | |
| 250℃，168 hr | 24 | % | |
| 250℃，336 hr | 28 | % | |
| 275℃，22 hr | 26 | % | |
| 275℃，70 hr | 33 | % | |
| 275℃，168 hr | 36 | % | |
| 275℃，336 hr | 53 | % | |
| MH | 0.418 | J | |
| ML | 0.113 | J | |
| t’50 | 2.1 | min | |
| t’90 | 5.2 | min | |
| ts2 | 3.2 | min |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |