| A range of high performance TPE compounds based on hydrogenated styrene block copolymer (H-SBC) specially formulated for applications requiring high strength and excellent abrasion resistance. Two ranges are offered, unfilled and filled. The unfilled versions offer the best properties with filled versions available as lower cost options Tensile strength for both types is mostly over 25% higher than comparable unfilled SEBS type compounds whilst DIN abrasion for all but the softest grades is two to three times better. The characteristic good compression set, heat ageing and low temperature properties are maintained whilst high levels of UV stability can be achieved with the correct choice of the appropriate masterbatch. For details please refer to our EvopreneTM General Information brochure.&& |
| Product Description | |
|---|---|
| Generic | SBC |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Weather resistance is good,Excellent Processability,Good heat aging resistance,Alkali resistant,Renewable resources,Ethanol tolerance,Food contact compliance,Acidproof,Block Copolymer,Good wear resistance |
| Availabilitys | North America,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.890 | g/cm³ | ISO 2782 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s A | 40 | ISO 868 | |
| Abrasion | 178 | mm³ | DIN 53516 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 5.50 | MPa | ISO 37 |
| 300% strain | 2.20 | MPa | ISO 37 |
| 200% strain | 1.80 | MPa | ISO 37 |
| 100% strain | 0.500 | MPa | ISO 37 |
| Tensile strain | |||
| fracture | 660 | % | ISO 37 |
| tear strength | 26 | kN/m | ISO 34-1 |
| Compression deformation | ISO 815 | ||
| 22℃，72 hr | 22 | % | ISO 815 |
| 70℃，22 hr | 35 | % | ISO 815 |
| 100℃，22 hr | 49 | % | ISO 815 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| M-S Flow | 0.883 | MPa | Internal Method |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Proposed maximum recycled material ratio | 20 | % | |
| Barrel rear temperature | 160 to 190 | °C | |
| Barrel middle temperature | 160 to 190 | °C | |
| Barrel front temperature | 160 to 190 | °C | |
| Nozzle temperature | 160 to 190 | °C | |
| Processing (melt) temperature | 250 | °C | |
| Mold temperature | 40 to 60 | °C | |
| Injection speed | Moderate | ||
| Vent depth | 0.020 to 0.050 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Method Ba, Angle (Unnicked) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |