| About |
|---|
| 15% Glass Reinforced, Toughened, PPA, High Performance Polyamide&& |
| Product Description | |
|---|---|
| Supplier | Celanese |
| Material Status | Commercial: Active |
| Features | Heat Stabilized |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Molding shrinkage | |||
| Parallel | 0.4 | % | ISO 294-4 |
| Normal | 0.7 | % | ISO 294-4 |
| Density | 10.4 | lb/gal | ISO 1183 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Modulus | |||
| Dry | 5520 | MPa | ISO 527 |
| Wet Cond | 5520 | MPa | ISO 527 |
| Creep, dry | 5506.2 | MPa | ISO 527 |
| Creep, wet cond | 5002.5 | MPa | ISO 527 |
| Tensile Stress | |||
| Broken BRK, dry dry | 131.1 | MPa | ISO 527 |
| Broken BRK, wet Cond | 103.5 | MPa | ISO 527 |
| Tensile Strain | |||
| Broken BRK, dry dry | 3.7 | % | ISO 527 |
| Broken BRK, wet Cond | 2.7 | % | ISO 527 |
| Flexural Modulus | 4905.9 | MPa | ISO 178 |
| Poisson’s ratio | |||
| Dry | 0.35 | ||
| Wet Cond | 0.35 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| Dry | 69.3 | kJ/m² | ISO 179/1eU |
| Wet Cond | 60.9 | kJ/m² | ISO 179/1eU |
| Charpy Notched Impact Strength | 60.9 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 300 | ℃ | ISO 11357-3 |
| Glass Transition Temperature | |||
| Dry | 115 | ℃ | ISO 11357-2 |
| Wet Cond | 65 | ℃ | ISO 11357-2 |
| Hot deformation temperature HDT | |||
| 1.8 MPa | 237.8 | ℃ | ISO 75-1/-2 |
| 0.45 MPa | 282.2 | ℃ | ISO 75-1/-2 |
| Coeff. of linear thermal expansion | |||
| Parallel, -40-23 ℃ | 0.178 | E-4/°F | ISO 11359-2 |
| Parallel | 0.16 | E-4/°F | ISO 11359-2 |
| Parallel, 55-160 ℃ | 0.111 | E-4/°F | ISO 11359-2 |
| Normal, -40-23 ℃ | 0.389 | E-4/°F | ISO 11359-2 |
| Normal | 0.389 | E-4/°F | ISO 11359-2 |
| Normal, 55-160 ℃ | 0.578 | E-4/°F | ISO 11359-2 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame Class Rating | |||
| 1.6 mm | HB | UL 94 | |
| 0.8 mm | HB | UL 94 | |
| Oxygen Index | 23 | % | ISO 4589-2 |
| FMVSS flame retardant rating | B | ISO 3795 | |
| Burning Speed | <80 | in/min | ISO 3795 |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Relative permittivity | |||
| 100Hz | 4.2 | IEC 62631-2-1 | |
| 1MHz | 3.9 | IEC 62631-2-1 | |
| Dissipation Factor | |||
| 100Hz | 55 | E-4 | IEC 62631-2-1 |
| 1MHz | 135 | E-4 | IEC 62631-2-1 |
| Volume Resistance | |||
| Dry | >1E13 | ohm·m | IEC 62631-3-1 |
| Wet Cond | >1E13 | ohm·m | IEC 62631-3-1 |
| Surface Resistivity | >1E15 | ohm | IEC 62631-3-2 |
| Electric strength | 419 | kV/in | IEC 60243-1 |
| Compared Tracking Index | |||
| Dry | 575 | IEC 60112 | |
| Wet Cond | 575 | IEC 60112 |
| Process Conditions | |||
|---|---|---|---|
| Injection Molding | Nominal value | Unit | Test method |
| Drying Temperature | 100 | ℃ | |
| Drying Time | 6-8 | hr | |
| Maximum Moisture Content | 0.1 | % | |
| Melt Temperature | 325 | ℃ | |
| Min Melt Temperature | 320 | ℃ | |
| Maximum Melt Temperature | 330 | ℃ | |
| Min Mold Temperature | 90 | ℃ | |
| Maximum Mold Temperature | 110 | ℃ | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. First Heat |
| 3. FMVSS 302 |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |