| Clyrell RC213M Clyrell RC213M is a high flow and highly modified polypropylene random copolymer. It contains anti-blocking additives. It does not contain Calcium Stearate. Clyrell RC213M is typically used by customers for manufacturing of oriented and un-oriented films. Typical applications reported by customers are lamination, metallized films, textile and packaging of foodstuffs. In addition, customers also reported that it is particularly suitable as a skin of multilayer twist film. Customers have been reporting that films produced using Clyrell RC213M offer a good balance of properties such as high clarity, brightness, stiffness and medium seal initiation temperature (SIT).&&Clyrell RC213M Polypropylene Random Copolymer Resin for Skin-layer of Co-extrusion Features: Excellent optical properties Wide hot tack range Low sealing temperature Applications: Skin layer of co-extruded cast film&& |
| Product Description | |
|---|---|
| Supplier | LyondellBasell |
| Generic | PP copolymer |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Good Clarity,Good surface appearance,Good heat sealing,Optical performance,High anti-blocking,Food contact compliance,Random copolymer,Low temperature heat sealing |
| Availabilitys | Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 10 | g/10min | ISO 1133 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Secant modulus | |||
| MD, 50 µ m, cast thin film | 660 | MPa | ASTM D882 |
| tensile strength | ASTM D882 | ||
| MD, yield, 50 µ m, extruded film | 22.0 | MPa | ASTM D882 |
| MD, fracture, 50 µ m, extruded film | 35.0 | MPa | ASTM D882 |
| Tensile strain | ASTM D882 | ||
| MD, yield, 50 µ m, extruded film | 10 | % | ASTM D882 |
| MD, fracture, 50 µ m, extruded film | 750 | % | ASTM D882 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 1.5 | kJ/m² | ISO 179/1eA |
| 23℃ | 3.4 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 65.0 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | |||
| A50 | 130 | ℃ | ISO 306/A50 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 50 µ m, cast thin film | 90 | ASTM D2457 | |
| Haze | |||
| 50 µ m, cast thin film | < 1.0 | % | ASTM D1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 66 | ISO 868 | |
| Tensile modulus | 1050 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 27.0 | MPa | ISO 527-2/50 |
| Tensile strain | ISO 527-2/50 | ||
| yield | 10 | % | ISO 527-2/50 |
| fracture | 600 | % | ISO 527-2/50 |
| friction coefficient | ASTM D1894 | ||
| With oneself – dynamic, casting thin films | 1.0 | ASTM D1894 | |
| Compared to itself – static, cast thin films | 1.0 | ASTM D1894 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.98 in/min |
| 3. 20 in/min |
| 4. Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |