| Fibremod GB215HP is a 20 % long glass fibre reinforced polypropylene grade intended for injection moulding and extrusion. The long glass fibres, chemically coupled to the polypropylene matrix, are providing outstanding mechanical properties such as high strength, high stiffness and excellent impact behaviour. Due to its excellent combination of properties this material can substitute in many applications other engineering plastics or metal alloys. A significant value of this material is the fact that it does not change its mechanical properties at humid conditions or water contact. The product is available in standard black 9502. Applications Fibremod GB215HP has been developed especially for demanding applications in the automotive industry. Dashboard carriers Structural seat parts Door module carriers Special Features Fibremod GB215HP is suitable for processing with special foaming technologies. High heat stabilised&& |
| Product Description | |
|---|---|
| Supplier | Borealis AG |
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | Good Rigidity,High impact resistance,Heat Stabilized |
| Availabilitys | Africa & Middle East ,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 2.0 | g/10min | ISO 1133 |
| Shrinkage rate | Internal Method | ||
| TD：2.0 mm | 0.55 | % | Internal Method |
| MD：2.0 mm | 0.10 | % | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| injection molding | 5300 | MPa | ISO 527-1-2 |
| tensile strength | |||
| Fracture, injection molding | 105 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, injection molding | 2.7 | % | ISO 527-2 |
| Bending modulus | |||
| injection molding | 4550 | MPa | ISO 178 |
| bending strength | |||
| injection molding | 130 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20 ℃, injection molding | 22 | kJ/m² | ISO 179/1eA |
| 23 ℃, injection molding | 19 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -20 ℃, injection molding | 32 | kJ/m² | ISO 179/1eU |
| 23 ℃, injection molding | 57 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -20 ℃, injection molding | 21 | kJ/m² | ISO 180-1A |
| 23 ℃, injection molding | 21 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 158 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | 125 | ℃ | ISO 306/B |
| Melt Energy | 72.5 | kJ/kg | ISO 11357 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| atomization | |||
| 16 hr，100℃ | 1.2 | mg | DIN 75201 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| discharge | 50.0 | µgC/g | VDA 277 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 2.0 | hr | |
| Processing (melt) temperature | 220 to 260 | °C | |
| Mold temperature | 30 to 50 | °C | |
| Hold pressure | 30.0 to 60.0 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |