| ELITE CS 6085B Enhanced Polyethylene Resin is an enhanced LLDPE ethylene-octene copolymer from Dow. This grade is a fully formulated resin designed for FFS and lamination films, combining excellent optical properties with improved mechanicals and an additive package designed to enhance COF stability. Complies with: U.S. FDA FCN 424 Europe Commission Regulation (EU) No 10/2011 Consult the regulations for complete details.&& |
| Product Description | |
|---|---|
| Supplier | DOW |
| Generic | EPE |
| Material Status | Commercial: Active |
| Availabilitys | Latin America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.918 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 1.0 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| friction coefficient | ASTM D1894 | ||
| With oneself – dynamic | 0.091 | ASTM D1894 | |
| With oneself – static | 0.11 | ASTM D1894 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 50 | µm | |
| Membrane puncture resistance | |||
| 50 µm | 6.62 | J/cm³ | Internal Method |
| Secant modulus | ASTM D882 | ||
| 2% secant, MD: 50 µ m | 165 | MPa | ASTM D882 |
| 2% secant, TD: 50 µ m | 170 | MPa | ASTM D882 |
| tensile strength | ASTM D882 | ||
| MD, yield, 50 µ m | 8.70 | MPa | ASTM D882 |
| TD, yield, 50 µ m | 9.40 | MPa | ASTM D882 |
| MD, fracture, 50 µ m | 30.3 | MPa | ASTM D882 |
| TD, fracture, 50 µ m | 28.8 | MPa | ASTM D882 |
| Tensile strain | ASTM D882 | ||
| MD, fracture, 50 µ m | 700 | % | ASTM D882 |
| TD, fracture, 50 µ m | 750 | % | ASTM D882 |
| Drop hammer impact | |||
| 50 µm | 640 | g | ASTM D1709-A |
| Elmandorf tear strength | ASTM D1922 | ||
| MD：50 µm | 920 | g | ASTM D1922 |
| TD：50 µm | 1200 | g | ASTM D1922 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45°，50.8 µm | 54 | ASTM D2457 | |
| Haze | |||
| 50.8 µm | 15 | % | ASTM D1003 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 239 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |