| Kingfa PVC-ZS40004 is a Polyvinyl Chloride material. It is available in Asia Pacific or North America for injection molding. Important attributes of Kingfa PVC-ZS40004 are: Eco-Friendly/Green Heat Resistant Non-Toxic Plasticized Typical applications include: Automotive Consumer Goods Handles Sporting Goods&& |
| Product Description | |
|---|---|
| Supplier | Kingfa |
| Generic | PVC, not specified |
| Material Status | Commercial: Active |
| Features | No DEHP plasticizer,Heat Resistance, Good,Nontoxicity |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.32 | g/cm³ | ASTM D792 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore A, 15 seconds | 91 | ASTM D2240 | |
| tensile strength | 18.5 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 190 | % | ASTM D638 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 60 to 80 | °C | |
| Drying time | 2.0 | hr | |
| Barrel rear temperature | 140 to 160 | °C | |
| Barrel middle temperature | 150 to 170 | °C | |
| Barrel front temperature | 160 to 180 | °C | |
| Processing (melt) temperature | 140 to 160 | °C | |
| Mold temperature | 30 to 50 | °C | |
| Injection speed | 慢to中等 | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 23°C |
| 3. 2.0 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |