| About |
|---|
| A post-consumer recycled polypropylene copolymer with enhanced flow properties for general use. Available in standard black (reference 90/04).&& |
| Product Description | |
|---|---|
| Generic | PP copolymer |
| Material Status | Commercial: Active |
| Features | Good liquidity,Copolymer |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.920 to 0.950 | g/cm³ | Internal Method |
| Melt Flow Rate | |||
| 230℃，2.16kg | 9.0 to 14 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield, 23 ℃ | > 18.0 | MPa | ISO 527-2/50 |
| Bending modulus | |||
| 23℃ | > 900 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | > 7.0 | kJ/m² | ISO 180-1A |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 1.0 to 2.0 | hr | |
| Recommended maximum moisture content | 0.050 to 0.10 | % | |
| Processing (melt) temperature | 190 to 220 | °C | |
| Mold temperature | 30 to 60 | °C | |
| Drying temperature | 80 | °C | |
| Drying time | 1.0 to 2.0 | hr | |
| Recommended maximum moisture content | 0.050 to 0.10 | % | |
| Melt temperature | 180 to 210 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |