| Stylac™ 191是一种丙烯腈丁二烯苯乙烯(ABS)产品,。 它,在非洲和中东、欧洲或亚太地区有供货。 特性包括: 阻燃/额定火焰 耐冲击&& |
| Product Description | |
|---|---|
| Supplier | Asahi Kasei |
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | High impact resistance,Good liquidity,HB |
| Availabilitys | Africa & Middle East ,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 220℃，10.0kg | 26 | g/10min | ISO 1133 |
| Melt Volume Rate | |||
| 220℃，10 kg | 26.9 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD | 0.40 to 0.60 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 22 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 80.1 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | 99.5 | ℃ | ISO 306/B |
| Relative temperature index | 60.0 | ℃ | UL 746 |
| Electrical performance | 60.0 | ℃ | UL 746 |
| Impact mechanical performance | 60.0 | ℃ | UL 746 |
| Ball pressure test | 85 | ℃ | EMAC |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 109 | ISO 2039-2 | |
| R-grade, 2.50 mm | 103 | ||
| tensile strength | |||
| yield | 44.8 | MPa | ISO 527-2/50 |
| Bending modulus | 2400 | MPa | ISO 178 |
| bending strength | 72.6 | MPa | ISO 178 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |