| Starflam RF0023E is a Mineral Flame Retardant Halogen Free Red and Phosphorous Free, Glass Fiber Reinforced, Polyamide 66 and Polyamide 6 Injection Molding Resin (eq. to RF1002Z230EM)&& |
| Product Description | |
|---|---|
| Supplier | Ascend |
| Generic | PA66/6 |
| Material Status | Commercial: Active |
| Features | V-2,V-0 |
| Availabilitys | Africa & Middle East ,Europe,Asia Pacific,Latin America,North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.73 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| MD：24 hrs | 0.20 to 0.50 | % | ISO 294-4 |
| Water absorption rate | |||
| 23℃，24hr | 0.80 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 94.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 1.5 to 2.5 | % | ISO 527-2 |
| Bending modulus | 7600 | MPa | ISO 178 |
| bending strength | 132 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 3.0 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 22 | kJ/m² | ISO 180/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 64 mm span | 178 | ℃ | ISO 75-2/Af |
| Vicat Softening Temp | |||
| B120 | 202 | ℃ | ISO 306/B120 |
| Thermal conductivity coefficient | 1.0 | W/m/K | ASTM E1530 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared to the leakage tracing index | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.80 mm | V-2 | UL 94 | |
| 1.70 mm | V-0 | UL 94 | |
| Glowing wire flammability index | |||
| 1.6 mm | 960 | ℃ | IEC 60695-2-12 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.20 | % | |
| Barrel rear temperature | 270 to 280 | °C | |
| Barrel middle temperature | 275 to 285 | °C | |
| Barrel front temperature | 280 to 300 | °C | |
| Processing (melt) temperature | 280 to 300 | °C | |
| Mold temperature | 60 to 90 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 80x10x4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |