Queo™ 8201LA

About
Queo 8201LA is an ethylene based octene-1 plastomer, produced in a solution polymerisation process using a metallocene catalyst. CAS-No.: 26221-73-8 Applications Queo 8201LA Demonstrated applications include: High strength flexible films Sound deadening sheets Additives Queo 8201LA contains a low amount of processing stabilizers Special Features Queo 8201LA is optimised to deliver: Versatile blending with other polyolefins in film, extrusion and moulding applications. High flexibility and surface softness High clarity Bridging of plastic and elastomeric properties Low temperature flex-cracking and impact resistance Outstanding toughness Low dielectric constant and dissipation factor Outstanding puncture resistance High filler and oil acceptance Low temperature impact strength&&

About

Queo 8201LA is an ethylene based octene-1 plastomer, produced in a solution polymerisation process using a metallocene catalyst. CAS-No.: 26221-73-8 Applications Queo 8201LA Demonstrated applications include: High strength flexible films Sound deadening sheets Additives Queo 8201LA contains a low amount of processing stabilizers Special Features Queo 8201LA is optimised to deliver: Versatile blending with other polyolefins in film, extrusion and moulding applications. High flexibility and surface softness High clarity Bridging of plastic and elastomeric properties Low temperature flex-cracking and impact resistance Outstanding toughness Low dielectric constant and dissipation factor Outstanding puncture resistance High filler and oil acceptance Low temperature impact strength&&

Product Description
Supplier	Borealis AG
Generic	乙烯基辛烯塑料
Material Status	Commercial: Active
Features	Good Clarity,Good flexibility,noise reduction,low-temperature impact resistance,Puncture Resistant
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.882	g/cm³	ISO 1183
Melt Flow Rate
190℃，2.16kg	1.1	g/10min	ISO 1133
ESCR(Environmental Stress Cracking Resistance)	> 1000	hr	ASTM D1693B

MECHANICAL	Nominal value	Unit	Test method
Shore hardness			ISO 868
Shaw’s A	85		ISO 868
Shaw’s D	< 30		ISO 868
tensile strength
fracture	23.0	MPa	ISO 527-2/5A
Tensile strain
fracture	730	%	ISO 527-2/5A
Bending modulus	23.0	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
23℃	No Break		ISO 180/1A

THERMAL	Nominal value	Unit	Test method
Embrittlement temperature	< -76.0	℃	ASTM D746
Vicat Softening Temp	51.0	℃	ISO 306/A
Melting temperature
DSC	75.0	℃	ISO 11357

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.