| SABIC® LLDPE PCG61 is a hexene-linear low density polyethylene typically used for healthcare applications. Films made from this resin exhibit good mechanical, optical and hottack properties. Application Typical application for SABIC® LLDPE PCG61 are pharmaceutical films, bags and pouches requiring good impact strength, tear resistance, optical performance and hottack properties. Compliance to Regulations SABIC® LLDPE PCG6118NE complies with the relevant monographs of the European Pharmacopoeia (EP) and the United States Pharmacopoeia (USPVI).&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Linear low density polyethylene |
| Material Status | Commercial: Active |
| Features | High impact resistance,Optical performance,Inoxidizability,Low density,Good tear strength,Hexene copolymers |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.918 | g/cm³ | ISO 1183/A |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.90 | g/10min | ISO 1133 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 50 | µm | |
| Tensile modulus | ISO 527-3 | ||
| MD, 50 µ m, blow molded film | 190 | MPa | |
| TD, 50 µ m, blow molded film | 230 | MPa | |
| tensile strength | ISO 527-3 | ||
| MD, yield, 50 µ m, blow molded film | 11.0 | MPa | |
| TD, yield, 50 µ m, blow molded film | 12.5 | MPa | |
| MD, fracture, 50 µ m, blow molded film | 47.0 | MPa | |
| TD, fracture, 50 µ m, blow molded film | 40.0 | MPa | |
| Tensile strain | ISO 527-3 | ||
| MD, fracture, 50 µ m, blow molded film | 630 | % | |
| TD, fracture, 50 µ m, blow molded film | 800 | % |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Izod notched impact strength | |||
| 50 µ m, blow molded | 350 | J/cm | ASTM D4272 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 106 | ℃ | ISO 306/A |
| Melting temperature | |||
| DSC | 124 | ℃ | Internal Method |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45 °, blow molded film | 57 | ASTM D2457 | |
| Haze | |||
| Blown film | 13 | % | ASTM D1003A |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Puncture resistance | |||
| Blow molded film, 50.0 µ m | 750 | J/m | Internal Method |
| tear strength | ISO 6383-2 | ||
| MD，50 µm | 100.0 | kN/m | |
| TD，50 µm | 400.0 | kN/m | |
| memo_intro |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Blown Film |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |