| About |
|---|
| Glass fibre reinforced and heat aging resistance injection moulding grade for industrial items such as gear wheels, solenoid valve housings, cable attachments, automotive fuel distributors and components for automotive gearshift. |
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Good heat aging resistance,Grease resistance |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.41 | g/cm³ | |
| Apparent density | 0.70 | g/cm³ | |
| Melt Volume Rate | |||
| 275℃，5 kg | 22.0 | cm³/10min | |
| Shrinkage rate | |||
| Restricted foaming | 0.40-0.45 | % | |
| TD | 1.1 | % | |
| MD | 0.4 | % | |
| Water absorption rate | |||
| Saturation, 23 ℃ | 5.0 to 5.5 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 11400 | MPa | |
| tensile strength | |||
| fracture | 200 | MPa | |
| Tensile strain | |||
| fracture | 3.1 | % | |
| Bending modulus | 10800 | MPa | |
| bending strength | 300 | MPa |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 8.0 | kJ/m² | |
| 23℃ | 10 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| -30℃ | 65 | kJ/m² | |
| 23℃ | 85 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 260 | ℃ | |
| 1.8 MPa, unannealed | 250 | ℃ | |
| Melting temperature | 260 | ℃ |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Polymer Abbreviation | PA66-GF35 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Processing (melt) temperature | 280 to 300 | °C | |
| Mold temperature | 80 to 90 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |