| The plasticized and impact modified PA12 grade UBESTA 3030 JI14L is equipped with a special low migration plasticizer offering high dimensional stability. The grade is stabilized against heat and weatherability. It is designed for high burst pressure performance at elevated temperatures as for brake systems in trucks with operating pressures of 12.5 bar.&& |
| Product Description | |
|---|---|
| Supplier | UBE |
| Generic | PA12 |
| Material Status | Commercial: Active |
| Features | Excellent Processability,High impact resistance,Good Dimensional Stability,Plasticizing,Heat Stabilized |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.01 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 235℃，2.16kg | 4.0 | g/10min | ISO 1133 |
| Shrinkage rate | ISO 294-4 | ||
| TD | 1.5 | % | |
| MD | 0.70 | % | |
| Water absorption rate | |||
| 23℃，24hr | 0.60 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40 ℃, completely fractured | 5.0 | kJ/m² | |
| 23 ℃, localized fracture | 90 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 96.0 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 45.0 | ℃ | ISO 75-2/A |
| Melting temperature | |||
| DSC | 175 | ℃ | ISO 3146 |
| Linear coefficient of thermal expansion | |||
| MD | 1.4E-4 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+13 | ohms·cm | IEC 60093 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 70 | ISO 868 | |
| Rockwell hardness | |||
| R-level | 69 | ISO 2039-2 | |
| tensile strength | |||
| yield | 32.0 | MPa | ISO 527-2 |
| Tensile strain | ISO 527-2 | ||
| yield | 19 | % | |
| fracture | 200 | % | |
| Bending modulus | 700 | MPa | ISO 178 |
| bending strength | 28.0 | MPa | ISO 178 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |