| About |
|---|
| polyamide 6.6, carbon fibre reinforced, wear and friction modified, heat stabilized&& |
| Product Description | |
|---|---|
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Lubricating,Heat Stabilized |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.51 | g/cm³ | ISO 1183 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 16000 | MPa | ISO 527-2 |
| tensile strength | 160 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 1.5 | % | ISO 527-2 |
| friction coefficient | ASTM G137 | ||
| Steel – Dynamic | 0.20 | ASTM G137 | |
| Steel – Dynamic | 0.22 | ASTM G137 | |
| Wear factor | ASTM G137 | ||
| 3.0 MPa，1.0 m/sec | 20 | 10^-8 mm³/N·m | ASTM G137 |
| 5.0 MPa，1.0 m/sec | 100 | 10^-8 mm³/N·m | ASTM G137 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 3.0 | kJ/m² | ISO 179-1eA |
| Charpy Unnotch Impact strength | 20 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 260 | ℃ | ISO 11357-3 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Usage Temperature – Long Time | |||
| < 130℃ | Yes | ||
| 130 to 200 ℃ | No | ||
| 200 to 260 ℃ | No | ||
| 260 to 300 ℃ | No |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 5 MPa, 1 m/s, dry |
| 3. 3 MPa, 1 m/s, dry |
| 4. Steel |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |