Hifax TYC 852X

About
Hifax TYC 852X very high melt flow , 2,000 MPa flexural modulus, mineral-filled, paintable thermoplastic elastomeric olefin (TEO) resin has an excellent balance of properties and processability. It w as designed primarily for automotive bumper fascias.&&

Product Description
Supplier	LyondellBasell
Generic	Polyolefin Elastomer
Material Status	Commercial: Active
Features	Good Rigidity,Excellent Processability,High impact resistance,High liquidity,Sprayable
Availabilitys	North America
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.06	g/cm³	ISO 1183
Melt Flow Rate	30	g/10min	ASTM D1238

MECHANICAL	Nominal value	Unit	Test method
tensile strength
yield	20.0	MPa	ISO 527-2
Bending modulus	2000	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch			ISO 180/1A
-40℃	3.5	kJ/m²	ISO 180-1A
23℃	35	kJ/m²	ISO 180-1A

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.