| About |
|---|
| PC 9381 10 FV is a medium viscosity polycarbonate (PC) resin and contains flame retardant agent, intended for injection moulding. The product is available in natural (PC 9381 10 FV) but other colours can be provided on request They combine high mechanical requiring rigidity, thermal and electrical properties with excellent chemical resistance and dimensional stability APPLICATIONS PC 9381 10 FV is intended for the injection moulding of electrical components and mechanical systems, such as: Electrical appliance components Lighting system Technical parts&& |
| Product Description | |
|---|---|
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good Dimensional Stability,Good Electrical Properties,Flame Characteristics,Solvent resistance,V-0 |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.27 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 300℃，1.2 kg | 13.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD | 0.20 to 0.50 | % | ISO 294-4 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.31 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| injection molding | 3400 | MPa | ISO 527-1-2 |
| tensile strength | |||
| Yield, injection molding | 55.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| Fracture, injection molding | 6.0 | % | ISO 527-2/50 |
| Bending modulus | |||
| injection molding | 3500 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 14 | kJ/m² | ISO 179/1A |
| Charpy Unnotch Impact strength | |||
| 23℃ | No Break | ISO 179/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 133 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 141 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | |||
| B50 | 142 | ℃ | ISO 306 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume resistivity | 1.0E+17 | ohms·cm | IEC 60093 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | V-0 | UL 94 | |
| Glowing wire flammability index | |||
| 2.0 mm | 960 | ℃ | IEC 60695-2-12 |
| Extreme oxygen index | 34 | % | ISO 4589-2 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Processing (melt) temperature | 290 to 310 | °C | |
| Mold temperature | 80 to 120 | °C | |
| Injection speed | Fast | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |