| Product Description | |
|---|---|
| Material Status | Commercial: Active |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.66 | g/cm³ | ISO 1183/A |
| Water Absorption | 0.02 | % | ISO 62 |
| Mold Shrinkage | |||
| MD | 0.2 | % | ISO 294-4 |
| TD | 0.6 | % | ISO 294-4 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Strength | 190 | MPa | ISO 527-1,-2 |
| Flexural Modulus | 1.7 | % | ISO 527-1,-2 |
| Flexural Strength | 280 | MPa | ISO 178 |
| Flexural Modulus | 12.0 | GPa | ISO 178 |
| Flexural Modulus | 2.4 | % | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 9 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | 45 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 280 | ℃ | ISO 11357 |
| Hot deformation temperature HDT | |||
| 1.82 MPa | ＞265 | ℃ | ISO 75-1,-2/A |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame Class Rating | |||
| 3.2 mm | V-0 | calss | UL 94 |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric Constant | |||
| 0.9 GHz | 4.1 | IEC 60250 | |
| 2.1 GHz | 4.0 | IEC 60250 | |
| 3.5 GHz | 3.9 | IEC 60250 | |
| Dissipation Factor | |||
| 3.5 GHz | 0.006 | IEC 60250 |
| Process Conditions | |||
|---|---|---|---|
| Injection Molding | Nominal value | Unit | Test method |
| Drying Temperature | 130 | ℃ | |
| Drying Time | 4 | hr | |
| Cylinder temperature | 280 – 330 | ℃ | |
| Mold Temperature | 130 – 150 | ℃ | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |