| About |
|---|
| TC-1600 A/B is an unfilled, low viscosity laminating epoxy resin for variety of fabricating applications. It features the ability to cure at room temperature for applications that do not require a working service temperature above 180°F (82?C). When post cured at elevated temperatures, this system can provide service up to 300°F (149°C). TC-1600 is commonly used to reinforce fiberglass, Kevlar/aramid, and carbon fiber fabrics. It is also used as an adhesive for bonding wood, composites, and other substrates. Adding fillers like fumed silica, micro-spheres, and short-strand fibers can create pastes for fillets, fairings, and bonding applications.&& |
| Product Description | |
|---|---|
| Generic | 环氧树脂 |
| Material Status | Commercial: Active |
| Features | Low Viscosity,Good bond |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| IMPACT | Nominal value | Unit | Test method |
| Notched impact strength of cantilever beam | 270 | J/m | ASTM D256 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 95 | ASTM D2240 | |
| tensile strength | |||
| yield | 241 | MPa | ASTM D638 |
| Bending modulus | 15900 | MPa | ASTM D790 |
| bending strength | 276 | MPa | ASTM D790 |
| compressive strength | 290 | MPa | ASTM D695 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.17 | g/cm³ | ASTM D792 |
| Density | |||
| Part A：25℃ | 1.147 | g/cm³ | |
| Part B：25℃ | 0.978 | g/cm³ | |
| Water absorption rate | |||
| 100hr | 1.5 | % | ASTM D570 |
| Shrinkage rate | 0.015 | % | |
| Brookfield viscosity | |||
| Mixing, 25 ℃ | 1.70 | Pa·s | |
| Part A，25℃ | 2.00 | Pa·s | |
| Part B，25℃ | 0.185 | Pa·s |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 121 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| MD | 2.0E-5 | 1/℃ | ASTM D3386 |
| Thermosetting components | |||
| Component A | 按重量计算的混合比: 100 | ||
| Component B | 按重量计算的混合比: 20 | ||
| Post curing time | 12 to 15 | hr | |
| stripping time | |||
| 25℃ | 12.0 to 15.0 | hr | |
| working hours | |||
| 25℃ | 30.0 | min |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Part B, 77°F |
| 3. Part A, 77°F |
| 4. Mixed |
| 5. Part B |
| 6. Part A |
| 7. 1 lb mass |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |