| 0309 exhibits a good balance of flow and melt strength for extrusion processes. The material demonstrates excellent heat and chemical resistance. The intended use of this product is for extruding monofilament/fibers. Available standard in powder (0309B4), pellet (0309P4) and crystallized pellet (0309C4) form.&& |
| Product Description | |
|---|---|
| Supplier | Celanese |
| Generic | PPS |
| Material Status | Commercial: Active |
| Features | Good liquidity,High Heat Resistance,Good melt strength,Solvent resistance |
| Availabilitys | North America,Latin America,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| THERMAL | Nominal value | Unit | Test method |
| Hot deformation temperature | |||
| 8.0 MPa, unannealed | 95.0 | ℃ | ISO 75-2/C |
| 1.8 MPa, unannealed | 115 | ℃ | ISO 75-2/A |
| 1.8 MPa, unannealed | 104 | ℃ | ASTM D648 |
| 0.45 MPa, annealed | 204 | ℃ | ASTM D648 |
| Glass transition temperature | 90.0 | ℃ | ISO 11357-2 |
| Melting temperature | 280 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| TD | 5.3E-5 | 1/℃ | ISO 11359-2 |
| MD | 5.2E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+7 | ohms·cm | ASTM D257 |
| Volume resistivity | 1.0E+11 | ohms·cm | IEC 60093 |
| Dielectric strength | 18 | kV/mm | ASTM D149 |
| Dielectric strength | 18 | kV/mm | IEC 60243-1 |
| Dielectric constant | ASTM D150 | ||
| 1 kHz | 3.00 | ASTM D150 | |
| 1 MHz | 3.00 | ASTM D150 | |
| Relative permittivity | |||
| 1 MHz | 4.60 | IEC 60250 | |
| Dissipation factor | ASTM D150 | ||
| 1 MHz | 1.1E-3 | IEC 60250 | |
| 1 kHz | 1.0E-3 | ASTM D150 | |
| 1 MHz | 9.0E-4 | ASTM D150 | |
| Arc resistance | 124 | sec | ASTM D495 |
| Compared to the leakage tracing index | 125 | V | IEC 60112 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 90.0 | MPa | ISO 527-2/1A/5 |
| Tensile strain | |||
| fracture | 8.0 | % | ISO 527-2/1A/5 |
| Bending modulus | |||
| 23℃ | 4200 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 145 | MPa | ISO 178 |
| Rockwell hardness | |||
| M-level | 93 | ASTM D785 | |
| M-level | 90 | ISO 2039-2 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.40 | g/cm³ | ASTM D792 |
| Density | 1.35 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| TD | 0.80 to 1.0 | % | ASTM D955 |
| MD | 1.0 to 1.2 | % | ASTM D955 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.020 | % | ISO 62 |
| Specific Heat Capacity of Melt | 1830 | J/kg/℃ | Internal Method |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 110 to 120 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Hopper temperature | 20 to 30 | °C | |
| Barrel rear temperature | 290 to 300 | °C | |
| Barrel middle temperature | 300 to 310 | °C | |
| Barrel front temperature | 310 to 320 | °C | |
| Nozzle temperature | 300 to 310 | °C | |
| Processing (melt) temperature | 310 to 320 | °C | |
| Mold temperature | 140 to 160 | °C | |
| Injection pressure | 40.0 to 80.0 | MPa | |
| Injection speed | Fast | ||
| Hold pressure | 30.0 to 60.0 | MPa | |
| Back pressure | 0.00 to 3.00 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |