| About |
|---|
| Product Description | |
|---|---|
| Supplier | Hyosung |
| Material Status | Commercial: Negative |
| Features | Low moisture absorption,Low Viscosity,High liquidity,Solvent resistance |
| Availabilitys | North America,Europe,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| tensile strength | |||
| yield | 60 | MPa | ASTM D638,ISO 527-1 |
| Tensile modulus | 1600 | MPa | ASTM D638 |
| Tensile modulus | 1500 | MPa | ISO 527-1 |
| Tensile yield elongation | 21 | % | ASTM D638,ISO 527-1 |
| Tensile strain at break | 300 | % | ASTM D638,ISO 527-1 |
| bending strength | 57 | MPa | ASTM D790,ISO 178 |
| Bending modulus | 1500 | ASTM D790 | |
| Bending modulus | 1400 | ISO 178 | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Notched impact strength of cantilever beam | N.B. | ASTM D256,ISO 180/1U | |
| Impact strength of cantilever beam notch | ASTM D256,ISO 180/1A | ||
| 23℃ | 95 | KJ/m² | ASTM D256 |
| 23℃ | 7 | KJ/m² | ISO 180/1A |
| -10℃ | 60 | KJ/m² | ASTM D256 |
| -10℃ | 4 | KJ/m² | ISO 180/1A |
| -30℃ | 40 | KJ/m² | ASTM D256 |
| -30℃ | 3 | KJ/m² | ISO 180/1A |
| Drop hammer impact | |||
| 23℃ | 50 | J | ISO 6603-2 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.24 | g/cm³ | ASTM D792,ISO 1183 |
| Shaw hardness | 77 | ISO 868 | |
| Rockwell hardness | 110 | ASTM D785 | |
| Water absorption rate | |||
| Balance, 50% RH | 0.5 | % | ASTM D570,ISO 62 |
| saturated | 2.1 | % | ASTM D570,ISO 62 |
| Melt Flow Rate | |||
| 240℃，2.16kg | 60 | g/10min | ASTM D1238 |
| 240℃，2.16kg | 56 | mL/10min | ISO 1133 |
| Shrinkage rate | |||
| MD, 3 mm | 2.0 | % | ASTM D955 |
| TD, 3 mm | 2.0 | % | ASTM D955 |
| MD, 2 mm | 1.6 | % | ASTM D955 |
| TD, 2 mm | 1.5 | % | ASTM D955 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 222 | ℃ | ASTM D955,ISO 11357 |
| Linear coefficient of thermal expansion | |||
| 25℃ to 55℃ | 9.7E-5 | ASTM E831 | |
| vicat softening point | |||
| 5 kg | 195 | ℃ | ASTM D-1525 |
| 50 N | 190 | ℃ | ISO 306/B50 |
| Hot deformation temperature | |||
| 66psi | 200 | ℃ | ASTM D648 |
| 264psi | 105 | ℃ | ASTM D648 |
| 0.45 MPa | 190 | ℃ | ISO 75 |
| 1.8 MPa | 92 | ℃ | ISO 75 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | |||
| Short term, 3 mm | 15 | kV/mm | ASTM D149 |
| Short term, 2 mm | 19 | kV/mm | ASTM D149 |
| Volume resistivity | 10E+14 | ohms·cm | ASTM D257 |
| Surface resistivity | 10E+17 | ohm/sq | ASTM D257 |
| Arc resistance | 130 | sec | ASTM D495 |
| Compared to the leakage tracing index | 600 | V | IEC 112 |
| Dielectric constant | |||
| 60Hz | 6.2 | ASTM D150 | |
| 60Hz | 5 | IEC 250 | |
| Dissipation factor | |||
| 60Hz | 0.008 | ASTM D150 | |
| 60Hz | 0.013 | IEC 250 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |