TABOREX® TA 1117 HD

About
A chemically-crosslinkable HDPE compound for the production of flexible pipes with an improved surface quality for domestic hot and cold water, under floor heating and central heating application. TABOREX-TA 1117 HD is a crosslinkable compound made by Silane grafted ethylene polymer. This graft polymer constitutes together with a TABOREX Masterbatch containing the crosslinking catalyst a “SIOPLAS-SYSTEM”. Pipes which are produced with the SILON grade TABOREX-TA 1117 HD fulfil the requirements of ASTM F876-04a, CSA 137.5-03, EN ISO 15875, BS 7291 and all related standards. This system allows the compound to be extruded as a normal thermoplastic polymer and will attain a high level of crosslinking in the processed form. The final product provides all the superior properties associated with crosslinked polyethylene.&&

About

A chemically-crosslinkable HDPE compound for the production of flexible pipes with an improved surface quality for domestic hot and cold water, under floor heating and central heating application. TABOREX-TA 1117 HD is a crosslinkable compound made by Silane grafted ethylene polymer. This graft polymer constitutes together with a TABOREX Masterbatch containing the crosslinking catalyst a “SIOPLAS-SYSTEM”. Pipes which are produced with the SILON grade TABOREX-TA 1117 HD fulfil the requirements of ASTM F876-04a, CSA 137.5-03, EN ISO 15875, BS 7291 and all related standards. This system allows the compound to be extruded as a normal thermoplastic polymer and will attain a high level of crosslinking in the processed form. The final product provides all the superior properties associated with crosslinked polyethylene.&&

Product Description
Generic	HDPE
Material Status	Commercial: Active
Features	Good flexibility,Crosslinked,High density
Availabilitys	Africa & Middle East ,North America,Asia Pacific,Europe
Process Methods	Extrusion

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.948	g/cm³	DIN 53479 , ASTM D1505
Apparent density	0.54	g/cm³	DIN 53466
Melt Flow Rate
190℃，5.0kg	1.0	g/10min	ASTM D1238，ISO 1133
water content	< 0.020	%
Volatiles	< 0.25	%	Internal Method
Gel content	70	%	EN 579

MECHANICAL	Nominal value	Unit	Test method
tensile strength
fracture	24.0	MPa	ISO 527-2
Tensile strain
fracture	450	%	ISO 527-2

Process Conditions
Extrusion	Nominal value	Unit	Test method
Drying temperature	80 to 90	°C
Drying time	2.0	hr
Barrel 1 zone temperature	160 to 170	°C
Barrel 2 zone temperature	170 to 180	°C
Barrel 3 zone temperature	170 to 190	°C
Barrel 4 zone temperature	170 to 190	°C
Head temperature	200 to 210	°C
Nozzle temperature	190 to 220	°C
Extruder Screw Temperature	70 to 90	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.