Borealis PP BB125MO

About
BB125MO is a heterophasic copolymer. This grade is a low melt flow rate grade intended for blow moulding and sheet extrusion, and features extremely good processability with improved melt strength and melt stability. As all polypropylenes, this grade shows excellent stress-cracking and chemical resistances. This polymer is one of the IMP (improved mechanical stability) grades, and is characterized by very high stiffness without any loss of impact strength even at low temperatures. CAS-No.: 9010-79-1 Applications Corrugated boards Industrial chemicals Special features Good melt strength Very high stiffness Good melt stability High impact strength Excellent stress crack resistance&&

About

BB125MO is a heterophasic copolymer. This grade is a low melt flow rate grade intended for blow moulding and sheet extrusion, and features extremely good processability with improved melt strength and melt stability. As all polypropylenes, this grade shows excellent stress-cracking and chemical resistances. This polymer is one of the IMP (improved mechanical stability) grades, and is characterized by very high stiffness without any loss of impact strength even at low temperatures. CAS-No.: 9010-79-1 Applications Corrugated boards Industrial chemicals Special features Good melt strength Very high stiffness Good melt stability High impact strength Excellent stress crack resistance&&

Product Description
Supplier	Borealis AG
Generic	PP copolymer
Material Status	Commercial: Active
Features	Good Rigidity,Excellent Processability,Low liquidity,High impact resistance,Good melt strength,Copolymer,Solvent resistance,low-temperature impact resistance,High ESCR,Higher melt stability
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.905	g/cm³	ISO 1183
Melt Flow Rate			ISO 1133
190℃，5.0kg	2.3	g/10min	ISO 1133
230℃，2.16kg	1.3	g/10min	ISO 1133
230℃，5.0kg	6.0	g/10min	ISO 1133

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus	1300	MPa	ISO 527-2/50
tensile strength
yield	25.0	MPa	ISO 527-2/50
Tensile strain
yield	5.0	%	ISO 527-2/50
Bending modulus	1200	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength			ISO 179/1eA
-20℃	7.0	kJ/m²	ISO 179/1eA
23℃	50	kJ/m²	ISO 179/1eA

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	85.0	℃	ISO 75-2/B

Process Conditions
Extrusion	Nominal value	Unit	Test method
Barrel 1 zone temperature	190 to 220	°C
Barrel 2 zone temperature	190 to 220	°C
Barrel 3 zone temperature	190 to 220	°C
Barrel 4 zone temperature	190 to 220	°C
Barrel 5 zone temperature	190 to 220	°C
Melt temperature	180 to 220	°C
Nozzle temperature	180 to 220	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.