| 玻璃填充的,非溴化/非氯化阻燃，基于环境可持续性的VALOX PBT树脂。基于EPEAT(电子产品环境评估工具)方法的消费后回收(PCR)使用率为31% |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | polybutylene terephthalate |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Flame Characteristics,Heat Stabilized |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Tensile modulus | 10420 | Mpa | ISO 527 |
| bending strength | |||
| Yield, 2 mm/min | 159 | Mpa | ISO 178 |
| Bending modulus | |||
| 2 mm/mim | 9350 | Mpa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Instrument control anti impact total energy 23 ℃ | 66 | cm-kgf | ASTM D 3763 |
| Notched impact strength of cantilever beam | |||
| 23℃，80*10*4 | 35 | kJ/m² | ISO 180/1U |
| -30℃，80*10*4 | 32 | kJ/m² | ISO 180/1U |
| Impact strength of cantilever beam notch | |||
| 23℃，80*10*4 | 6 | kJ/m² | ISO 180-1A |
| -30℃，80*10*4 | 5 | kJ/m² | ISO 180-1A |
| Charpy Notched Impact Strength | |||
| 23 ℃, 80 * 10 * 4, 62mm span | 5 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 200 | ℃ | ASTM D1525 |
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 64 mm span | 190 | ℃ | ISO 75/Af |
| 1.8 MPa, unannealed, 3.2 mm | 190 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| MD：-40~150℃ | 2.3E+01 | 1/℃ | ASTM E831 |
| TD：-40~150℃ | 7.8E+01 | 1/℃ | ASTM E831 |
| Linear coefficient of thermal expansion | |||
| MD：30~80℃ | 2.8E+01 | 1/℃ | ISO 11359-2 |
| TD：-30~80℃ | 1.05E+01 | 1/℃ | ISO 11359-2-2 |
| Vicat Softening Temp | |||
| B50 | 200 | ℃ | ISO 306 |
| B120 | 200 | ℃ | ISO 306 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.53 | g/cm³ | ASTM D792 |
| Density | 1.52 | g/cm³ | ISO 1183 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.25 | % | ISO 62 |
| 23℃，50% RH | 0.07 | % | ISO 62 |
| Melt Volume Rate | |||
| 250℃，5 kg | 15 | cm³/10min | ISO 1133 |
| Melt Flow Rate | |||
| 250℃，5.0kg | 20 | g/10min | ASTM D1238 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot wire ignition {PLC} | 0 | PLC Code | UL 746A |
| High current arc ignition (surface {PLC}) | 0 | PLC Code | UL 746A |
| Compared to the leakage tracing index | 2 | PLC Code | UL 746A |
| Compared to the leakage tracing index | 275 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Glowing wire flammability index | |||
| 850 ℃, passed through | 0.8 | mm | IEC 60695-2-12 |
| Igniting temperature of the hot wire | |||
| 3 mm | 800 | ℃ | IEC 60695-2-13 |
| Process Conditions | |||
|---|---|---|---|
| Injection molding | Nominal value | Unit | Test method |
| Drying temperature | 110-120 | °C | |
| Drying time | 2-4 | hrs | |
| Maximum water content | 0.02 | % | |
| Melt temperature | 245-260 | °C | |
| Nozzle temperature | 230-255 | °C | |
| Front temperature | 240-260 | °C | |
| Mid section temperature | 235-250 | °C | |
| Post stage temperature | 230-240 | °C | |
| Hopper temperature | 40-60 | °C | |
| Mold temperature | 40-100 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |