| Extrusion Grade ABS&& |
| Product Description | |
|---|---|
| Supplier | EnCom |
| Generic | ABS |
| Material Status | Commercial: Active |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.03 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 200℃，10.0kg | 13 | g/10min | |
| 200℃，5.0kg | 1.4 | g/10min | |
| Shrinkage rate | |||
| MD：3.2 mm | 0.40 | % | |
| TD：3.2 mm | 0.40 to 0.70 | % | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 640 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 96.7 | ℃ | ASTM D648 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 108 | ASTM D785 | |
| tensile strength | |||
| yield | 38.6 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 4.4 | % | ASTM D638 |
| Bending modulus | 1790 | MPa | ASTM D790 |
| bending strength | 57.9 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 82 to 93 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.10 | % | |
| Barrel rear temperature | 188 to 232 | °C | |
| Barrel middle temperature | 204 to 246 | °C | |
| Barrel front temperature | 218 to 260 | °C | |
| Nozzle temperature | 218 to 274 | °C | |
| Processing (melt) temperature | 218 to 274 | °C | |
| Mold temperature | 32 to 71 | °C | |
| Back pressure | 0.172 to 0.689 | MPa | |
| Screw speed | 25 to 75 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |