| About |
|---|
| SABIC® LLDPE 118NE is a butene linear low density polyethylene resin typically used for general purpose applications. Films produced from this resin are tough with good puncture resistance, high tensile strength, good hottack properties and low gel levels. SABIC® LLDPE 118NE is TNPP free. Application Typical applications for SABIC® LLDPE 118NE are shipping sacks, ice bags, frozen food bags, liners, carrier bags, garbage bags, agriculture films, lamination and coextruded films, shrink film (for blending with LDPE), industrial consumer packaging and high clarity film if blended with (10-20%) LDPE. This product is not intended for and must not be used in any pharmaceutical/medical applications.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Linear low density polyethylene |
| Material Status | Commercial: Active |
| Features | Low speed solidification point,Inoxidizability,Good Tensile Strength,Low density,Butylene copolymer,Puncture Resistant |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.918 | g/cm³ | ISO 1183/A |
| Melt Flow Rate | |||
| 190℃，2.16kg | 1.0 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| friction coefficient | |||
| Blown film | 1.2 | ASTM D1894 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 50 | µm | |
| Tensile modulus | ISO 527-3 | ||
| MD, 50 µ m, blow molded film | 190 | MPa | |
| TD, 50 µ m, blow molded film | 210 | MPa | |
| tensile strength | ISO 527-3 | ||
| MD, yield, 50 µ m, blow molded film | 11.0 | MPa | |
| TD, yield, 50 µ m, blow molded film | 12.0 | MPa | |
| MD, fracture, 50 µ m, blow molded film | 44.0 | MPa | |
| TD, fracture, 50 µ m, blow molded film | 33.0 | MPa | |
| Tensile strain | ISO 527-3 | ||
| MD, fracture, 50 µ m, blow molded film | 650 | % | |
| TD, fracture, 50 µ m, blow molded film | 850 | % |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Izod notched impact strength | |||
| 50 µ m, blow molded | 230 | J/cm | ASTM D4272 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 103 | ℃ | ISO 306/A |
| Melting temperature | |||
| DSC | 121 | ℃ | Internal Method |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45 °, 50.0 µ m, blow molded film | 53 | ASTM D2457 | |
| Haze | |||
| 50 µ m, blow molded film | 13 | % | ASTM D1003A |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Blocking force | |||
| Blow molded film, 50.0 µ m | 10 | g | Internal Method |
| Puncture resistance | |||
| Blow molded film, 50.0 µ m | 630 | J/m | Internal Method |
| Re blocking – blow molded film (50.0 µ m) | 65 | g | Internal Method |
| tear strength | ISO 6383-2 | ||
| MD，50 µm | 40.0 | kN/m | |
| TD，50 µm | 140.0 | kN/m | |
| memo_intro |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Blown Film |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |