| SABIC® LDPE 2201H3W is a grade anti block and slip agent (E=erucamide). The grade has very good draw down ability. Films based on 2201H3W combine toughness with high tear strength, good optical properties and low CoF. Application SABIC® LDPE 2201H3W is typically used for thin packaging film purposes, where good optical properties are required. SABIC® LDPE 2201H3W can typically be used for food applications due to very low migration levels. This product is not intended for and must not be used in any pharmaceutical/medical applications.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | LDPE |
| Material Status | Commercial: Active |
| Features | Good flexibility,Smoothness,Good dissection,Optical performance,Low coefficient of friction,High anti-blocking,Low density,Good tear strength,Low to no mobility |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.922 | g/cm³ | ISO 1183/A |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.85 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| friction coefficient | |||
| Blown film | 0.20 | ASTM D1894 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 50 | µm | |
| Tensile modulus | ISO 527-3 | ||
| MD, 50 µ m, blow molded film | 170 | MPa | |
| TD, 50 µ m, blow molded film | 170 | MPa | |
| tensile strength | ISO 527-3 | ||
| MD, yield, 50 µ m, blow molded film | 11.0 | MPa | |
| TD, yield, 50 µ m, blow molded film | 11.0 | MPa | |
| MD, fracture, 50 µ m, blow molded film | 27.0 | MPa | |
| TD, fracture, 50 µ m, blow molded film | 22.0 | MPa | |
| Tensile strain | ISO 527-3 | ||
| MD, fracture, 50 µ m, blow molded film | > 200 | % | |
| TD, fracture, 50 µ m, blow molded film | > 500 | % |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Izod notched impact strength | |||
| 50 µ m, blow molded | 250 | J/cm | ASTM D4272 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 96.0 | ℃ | ISO 306/A |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45 °, 50.0 µ m, blow molded film | 68 | ASTM D2457 | |
| Haze | |||
| 50 µ m, blow molded film | 8.0 | % | ASTM D1003A |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Blocking force | |||
| Blow molded film, 50.0 µ m | g | Internal Method | |
| Re blocking – blow molded film (50.0 µ m) | 10 | g | Internal Method |
| tear strength | ISO 6383-2 | ||
| MD，50 µm | 45.0 | kN/m | |
| TD，50 µm | 35.0 | kN/m | |
| memo_intro |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Blown Film |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |